Electronics Forum | Mon Oct 15 10:51:49 EDT 2001 | davef
On over printing, the general issues are: * Paste deposits being so large that when reflowing, collapse onto many, rather than a single solder mass. * Paste expanding during heating and being close to other solder deposits and bridging [as you say].
Electronics Forum | Mon Nov 15 12:13:41 EST 1999 | Dave F
Steve: There are guidelines for determining if your aperture has the correct proportions to the foil thickness. Maybe that�s what you�re looking for: 1 Aspect ratio = aperture width/foil thickness Chemically etched SB GT 1.5 Laser cut SB GT 1.2
Electronics Forum | Mon Nov 15 12:09:55 EST 1999 | Dave F
Steve: Continuing with Dan�s thinking, generally, "poor release" (paste hanging-up in the stencil holes) could have three main (or combination of) causes: 1 Equipment: Stencil is too thick. Specifically, your 0.006 should be OK, providing you don�
Electronics Forum | Thu May 24 09:11:12 EDT 2001 | Grant Petty
Hi, I would agree. We purchased a TP9 just the slow machine, but we were a small company at the time, and it worked fantastic. Almost no maintenance, and it's a dream to changeover. The serivce in Australia is also very good, but that does not appl
Electronics Forum | Wed Aug 29 03:16:20 EDT 2018 | cannizzaro
It is recommended that the thickness of the stencil of 0.1mm, the steel mesh should be partially nano-coated. It is best not to dry easily, and the particles are not easy to be too large. I have tried ALLPCB for this kind of BGA in the past and they
Electronics Forum | Tue Aug 22 03:04:07 EDT 2006 | PP
Any help/suggestion is much appreciated I am doing lots of BGA Reworks from a small uBGA with a few balls to a large BGA with over 1500 balls. The reworks have been done on SRT 1100 Series Machine for many years. SRT 1100 Machine is good for the c
Electronics Forum | Mon Nov 12 16:14:47 EST 2001 | davef
Yes!!! How can we assemble boards with 20 pitch when we allow 0.008� error to the master art? Excellent question!!! IPC-D-300G has nothing to do with assembler requirements. It is written by and for fabricators, so that they can be comfortable.
Electronics Forum | Mon Jul 15 09:41:11 EDT 2002 | soupatech
I am experimenting with 2 types, FG256 17x17mm and FG456 23x23mm both with a 1mm pitch and .5mm ball. They both have a full array. As for as the x-ray, we are looking into pruchasing some used equipment but will mostly send them out for testing until
Electronics Forum | Fri Oct 22 06:19:42 EDT 1999 | TNT
Ron, if I am reading this correctly the 20mil parts are not having problems on a 6mil stencil. If you increase the entire thickness of the stencil to 8mils, there should not be any issues with the 20mil components. The supports you are using could p
Electronics Forum | Fri Aug 24 13:21:59 EDT 2018 | babe7362000
What do others use as far as solder paste type, stencil thickness and aperature size for a .4mm Ball Pitch CSP. Ball diameter is .3mm. Please let me know your thoughts or what you use. Thanks