Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Fri Jan 27 17:23:10 EST 2006 | muse95
Watch the solder profiles allowed for these caps. Most electrolytics cannot withstand high heat. Even RoHS compliant Electrolytics are often rated for peak 245C, 3 secs max, for example. Nowhere close to the 260C 10-20 sec you usually like to see.
Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN
I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f
Electronics Forum | Tue Aug 31 19:17:43 EDT 2004 | russ
Now see Dave, now I have some good info on why it is "bad", This must be the lead enrichment I have heard about but never got any substantiated data or explanantion. I wonder how much weaker or less reliable these are. Is there any data that you k
Electronics Forum | Thu May 06 06:47:12 EDT 2004 | praveen
Hi, I just need to undestand any issue? If I mount Pb free BGA and use normal SN/Pb solder paste?
Electronics Forum | Wed Jun 02 19:01:50 EDT 2004 | lynnmc
Thanks to all on this feedback
Electronics Forum | Tue Jun 01 17:37:34 EDT 2004 | lynnmc
Any view on what the minimum reflow temperature is for a SAC ball bga to form a reliable joint with PbSn solder?
Electronics Forum | Thu May 06 08:59:25 EDT 2004 | davef
Even with PbSn solderpaste the leadfree BGA's have a superior resistance to solder-joint fatigue failure when compared to conventional parts. [Solder Fatigue Reliability Issues in Lead Free BGA Packages, Pedro Chalco of IBM, Pan Pacific Microelectron
Electronics Forum | Tue Jun 01 19:25:19 EDT 2004 | Ken
...oops part 2: I will assume a sac 350 ball??? 217-218C this will completely reflow the ball and form a "normalized" joint with a collapsed structure.
Electronics Forum | Tue Jun 01 19:23:15 EDT 2004 | Ken
profile it for the tin/lead paste. The tin in the solder paste will begin to disolve the sac ball. This is exactly the same scenario as 90/10 (80/20)high temp balls found on ceramic bga and many super bga devices (except the sac balls are now tin r