Electronics Forum | Wed Oct 13 15:45:04 EDT 2021 | dilogic
Does anybody have experience with ATF's selective soldering machines? Information on the web is scarce and their responses to my queries are either none or very limited. Any information is welcome...
Electronics Forum | Thu Nov 03 09:43:55 EST 2005 | lupo
Check flux penetration and type of flux. How much is solid contents. The solder filling is better under Nitrogen. Check the time (speed) of the nozzle whether is correct. Usually For SAC305 the temperature of bath is 320C/degrees, but only for sel
Electronics Forum | Thu Jun 25 11:11:13 EDT 2009 | bruna
Hello, I want to hear some experience about selective soldering for PCB using nozzle plate and screens Do you have solder defects? bridges and insufficient soldering? How do you combat that? and about the screens you have good quality? What is the f
Electronics Forum | Sun Jul 04 13:27:31 EDT 2021 | dilogic
We are looking for new entry-level selective soldering machine. I would appreciate if you can share experience with the equipment you have, as there are many machines on the market and it's a though choice. We will use it for lead-free soldering and
Electronics Forum | Thu May 20 09:28:21 EDT 2004 | Joe N>
Take a look at Ersa at http://www.jdnoble.com
Electronics Forum | Wed May 26 18:54:10 EDT 2004 | Dreamsniper
PILLARHOUSE RUBY, EMERALD atc.
Electronics Forum | Wed May 26 20:21:32 EDT 2004 | longpham246
Try Dover/Soltec and contact Larry at Lapa Enterprise.
Electronics Forum | Wed Nov 02 11:25:46 EST 2005 | dougm
I should specify that I am using SAC 305 as well.
Electronics Forum | Mon Dec 20 08:26:17 EST 1999 | pascal MATHIEU
hello guys ; we are using some standard selective wave soldering unit used in lined ; the drawback of a such machine is 1/the speed which is quiet low (the board is coming on position through the conveyor, then the head delivering the solder moves s
Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap