Electronics Forum | Thu Jan 27 16:43:15 EST 2005 | russ
Ther is a solder alloy out there that is supposed to allow lead free wave processing without having to upgrade pumps and such or increasing the pot temp (direct drop in). I have not used it nor do I plan on doing leadfree wave soldering but you may
Electronics Forum | Wed Jan 26 17:36:22 EST 2011 | ck_the_flip
had a quick question regarding compatibility of Sn100C HASL finish and regular Sn63 solder paste. Does the thermal profile have to reach Sn100C eutectic temps. in order for the Sn 100C HASL to coaelesce with the Sn63 Solder paste? How reliable is t
Electronics Forum | Fri Mar 31 12:27:27 EST 2006 | Marcus
We have used the SN100C for over a year now with fanastic results. We use the SAC305 for SMT and SN100C wire exclusively. There are no problem mixing the alloys. I am also on the commitee for the NASA testing. The SN100C did out perform SAC and SnPb
Electronics Forum | Fri Feb 04 16:07:38 EST 2011 | pjc
If your peak temps in profiling the Sn/Pb solderpaste are 210C-215C, then no, you will not "weld" to the SN100C finish. SN100C is liquidus at 227C, too hot for most Sn/Pb solderpastes.
Electronics Forum | Tue Oct 03 22:48:21 EDT 2006 | C.K. the Flip
It sounds as if this Sn100c HASL process is still in its infancy requiring further process development and characterization..weather its a better more active flux or a different profile... Given your situation of the Sn100c coating actually "repellin
Electronics Forum | Wed Mar 18 16:50:20 EDT 2009 | khowell
There are many users of SN100C in reflow. SN100C was originally introduced as a wave solder alloy which offered cost savings over SAC, no solder pot erosion, and high fluidity. Since it is eutectic, no plastic range, the joints have a smooth, shiny
Electronics Forum | Tue Jan 17 21:40:08 EST 2012 | gaz
I'm testing SN100C, and with our 5 zone oven I seem to be able to fix one issue by changing the profile, but that might introduce a new problem. Some profiles work very well on most components, but have issues on other components. These are usually 0
Electronics Forum | Thu Feb 24 00:37:08 EST 2022 | joshsvoboda
I have a pcb with an ENIG finish that is using a 144 pin LQFP and being soldered withSN100C/NC258 T4 paste. I used a oven profiler where the probes are taped down to the joint and the profiling software adjusts the program for the best profile for
Electronics Forum | Mon Jan 23 19:48:27 EST 2012 | gaz
This make me curious how many people are using sn100 versus how many using sac305. The sn100 seemed to generally cover the pads and flow a little better, and looked nicer, but SAC305 overall was easier. Is this normal or do I need to work more on sa
Electronics Forum | Fri Apr 07 17:44:07 EDT 2006 | ratsalad
I still have half of a 500 g jar of this paste left. I'm going to give it another shot, but my first experience was not so wonderful. Everything was great until we reflowed it. Our profile matched AIM's recommendation, as far as I can see. The ch