Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Mon May 14 17:12:20 EDT 2001 | davef
Continuing along the path that Brian took ... IPC-7525 gives design guideline for stepped stencils. It goes something like: * Stepped area SB GT 25 thou from pads located on the greatest thickness of the stencil * Pads in stepped area SB GT 35 tho
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Thu Mar 11 10:31:57 EST 1999 | Justin Medernach
| NASA CommQuest | | | Photopolymerized Conducting Polymers | | Directions: | 1.Please read the information provided on this technology. You may follow the links to additional information resources below. | | 2.After evaluating the technology,
Electronics Forum | Thu Aug 06 09:51:20 EDT 1998 | Bob Willis
This text may be of interest to any one with tin lead spots Guide to Solder Spots - A New Plague in Manufacture ? So what are solder spots ? They appear to be the next big problem in modern reflow assembly in fact in any process that involves solder