Electronics Forum | Mon Nov 12 16:14:47 EST 2001 | davef
Yes!!! How can we assemble boards with 20 pitch when we allow 0.008� error to the master art? Excellent question!!! IPC-D-300G has nothing to do with assembler requirements. It is written by and for fabricators, so that they can be comfortable.
Electronics Forum | Wed Oct 10 13:51:08 EDT 2007 | petep
Coilcraft has posted the following and I am wondering how you folks are handling the use of coils in a Water Soluble world. PCB Washing and Coilcraft Parts Coilcraft tests for resistance to solvents per the following specification: Resistance to s
Electronics Forum | Wed Mar 07 12:57:55 EST 2018 | aemery
Gerber EZ is not available on the Accuflex platform. Speedline (now ITW EAE), like most manufactures, do not want to offer new tools on old platforms. There is one feature in the AccuPro software that I don't believe was added in any version of the
Electronics Forum | Mon Jun 08 14:19:30 EDT 1998 | Gary Simbulan
Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Electronics Forum | Thu Jun 05 16:44:19 EDT 2003 | blnorman
The data we have is from an IBM report. Below 100�C the SAC reliability is almost double that of SnPb (-40 to 100�C thermal cycle). When the upper end temp is increased to 125�C the reliability drops to 75% of SnPb. I'd like to see the data that s
Electronics Forum | Thu Dec 10 03:37:29 EST 1998 | Youngho Song
Hi everybody? I heard that typical FR-4 would not acceptable for BGA application. What is the main reason? (thermal property? or CTE?) Sombody please answer me the requirement of PCB substrate for PCB application. Thanks. Youngho Song
Electronics Forum | Mon Jun 20 10:59:18 EDT 2005 | Jason Fullerton
Extra cooling is better (Alpha recommends -3 to -7 degC/sec) for cosmetics. Less chance of s o called 'cooling lines' that look similar to 'cold' tin-lead joints. (Seems a bit steep to me - I worry about the risk of cracking ceramic caps.) Might be
Electronics Forum | Thu Dec 10 09:09:31 EST 1998 | Earl Moon
| Hi everybody? | I heard that typical FR-4 would not acceptable for BGA application. | What is the main reason? | (thermal property? or CTE?) | Sombody please answer me the requirement of PCB substrate for PCB application. | Thanks. | | Youngho Son
Electronics Forum | Tue Jul 19 08:26:46 EDT 2016 | pavel_murtishev
Aleksander, The answer is no. Solder deposit being printed is 80um-150um in height depending on PCB design what is two times higher than any track covered by solder mask. Molten solder will merely center the component. QFNs are prone to soldering
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830