Electronics Forum | Mon Dec 13 00:05:28 EST 1999 | Dennis O'Donnell
I can't figure out why everyone is plating everything with gold. According to the J Standard, gold plating should be removed before soldering to the surface. The gold, when left on the surface to be soldered will contaminate the solder joint and ca
Electronics Forum | Wed Jul 12 11:26:12 EDT 2006 | flipit
Hi, I believe you have classic gold imbrittlement here. With 80 microinches of gold you are way over the limit. You can try to reflow longer time and at a higher temperature. The gold does not melt into the solder joint. The gold dissolves into
Electronics Forum | Fri Nov 10 17:44:48 EST 2000 | Dave F
In response to your questions: Is the embrittlement from excess gold in lead / tin solder connections bad? It can be vereeee bad. Does it affect all plating processes the same? Give us a break and read the SMTnet Archives, for instance: BGA prob
Electronics Forum | Fri Feb 28 01:36:43 EST 2020 | crystal12
> What is the use of gold plated boards? <BR> <BR> With the increasing integration of IC, the more IC the more dense. The vertical tin spray process is difficult to flatten the pads, which brings difficulty to the SMT mounting, and
Electronics Forum | Mon Dec 13 10:12:45 EST 1999 | John Thorup
Hi Dennis The gold plating on a circuit board is present to protect the nickle plating from corrosion. The layer is so thin that as it goes into solution in the solder it constitutes only a small percentage of the total joint. It is commonly accept
Electronics Forum | Fri Oct 05 18:59:53 EDT 2001 | Dan Steffler
I have had an issue where solder has contaminated gold plated pads (fingers) where it is not acceptable. The pads must remain perfectly coplaniar for a LCD zebra strip to lay accross them. Does anyone know of a way to remove the marriage level of s
Electronics Forum | Mon Mar 20 09:24:38 EST 2000 | John Sipper
1. Spec references for max allowable untinned gold near glass seal and case body? 2. Low cost mechanical dip system to facilitate tinning of DIP parts. (Low volume; currently using hand solder iron techniques to allow for max coverage without bridg
Electronics Forum | Sun Apr 24 09:12:00 EDT 2005 | davef
We're not sure what your customer is talking about either. Gold and tin form an intermetallic compound [IMC] that can cause poor solder connections. To minimize the potential of a problem, keep gold to less than 3 percent of the metal. [Search the
Electronics Forum | Sat Apr 14 09:28:58 EDT 2007 | davef
When soldering a component to a board, the solderability protection on the component combines with the solderability protection on the board and the solder to form an alloy. This alloy is unique for that combination of solder and solderability protec
Electronics Forum | Tue May 19 12:54:55 EDT 1998 | Richard Jackson
| We had a similar problem. But whenever the solder came from the screen printer the solder would wet to the gold fingers, with the help of residual flux. But the problem is balls, that I assume are not wetted to the gold fingers but instead are jus