Electronics Forum | Wed Jul 30 16:16:19 EDT 2003 | swagner
What is the industry standard for wave and selective solder PPM defect rate for a world class facility, any responses are appreciated.
Electronics Forum | Fri May 14 09:00:35 EDT 2010 | rafacadiz
I attached a RX picture. A lot of voids and micro balls arround the flux residue. What do you think, relow temperature reflow or OSP poor weeting.? I appreciate your comments. Thanks,
Electronics Forum | Mon Dec 02 17:02:28 EST 2002 | Vince Whipple
Steve, I agree with the recommendation to check the temperature. This is the first place to go. Is this an IPA or water based Noclean? What is the topside temp of the assembly at the effected areas? If you are too cold you will have a tendency to hav
Electronics Forum | Wed Aug 10 12:05:11 EDT 2005 | Rob
Hi Pr, No idea what the material is - we haven't usd it for a while now, but it was flush & didn't cause any printing problems on double sided reflow. Your board house should know all about it - I would suggest some but ours are all UK or China/Tai
Electronics Forum | Mon Dec 02 16:19:11 EST 2002 | slthomas
Unfortunately it's nc or we'd be worrying about this on the fly. Non-contact is defintely and issue....this is an 18"x9" board with 1500 bottom side SMT parts that are scattered among the through-hole and vice-versa. We're currently using 7 hold-
Electronics Forum | Tue Aug 09 13:25:24 EDT 2005 | pr
From what I can gather, the annular rings are used for grounding when these boards are put in housings. A screw goes through the hole and is torqued down. If there is excess solder on the annular ring, the screw doesn't seat properly. The pallets cov
Electronics Forum | Fri Apr 06 08:28:34 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Protective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyamide with electroptical connectio
Electronics Forum | Fri Apr 06 08:27:09 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Proctective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyimide with electroptical connecti
Electronics Forum | Mon Dec 02 12:52:40 EST 2002 | slthomas
We're trying a selective soldering pallet for the first time with mixed reviews. Are solder balls a prevalent problem with this process? Most of them seem to correspond with pallet wall locations....is it too much turbulence from the rotary chip wav
Electronics Forum | Mon Dec 16 16:35:55 EST 2002 | Jim Ferris
Randy, Steve & all, Can you guys point me in the right direction when it come to using selective wave soldering...I am trying to get in-depth information on the Pro's & Con's of having our supplier use this process for our PWA's. (I can see there ar