Electronics Forum | Wed Feb 24 11:28:09 EST 2010 | vleasher
I apologize for being so vague. It is a standard leaded process using ALPHA OM-5100 for the SMT. So would a reduction in wash temp result in less white residue?
Electronics Forum | Fri Dec 01 14:12:50 EST 2000 | Jim M.
My company currently uses water soluble paste for our SMT process. We were having trouble retaining hot water in our in line, closed loop DI cleaner. The cleaner kept shutting down when the water temp. dropped below 125C. As a result, the conveyor
Electronics Forum | Mon Jan 26 11:46:16 EST 1998 | Rin Or
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Mon Jan 19 20:25:52 EST 1998 | Steve Gregory
| I have a problem! The solder on my pc boards look great comeing out | of my reflow oven. They go thrue the rest of the prossese | and at the end at the qc station it's cold or whitish or gray not shiny. | does any one have a idea on how to correct
Electronics Forum | Wed Feb 24 10:23:04 EST 2010 | xps
60° C). Moreover (by IPC standard)... "White residues resulting from no-clean or other processes are acceptable provided the residues from chemistries used have been qualified and documented as benign...". So, use an EDX or IC analysis in order to
Electronics Forum | Thu Feb 25 03:37:25 EST 2010 | xps
Sorry, but I don't know this brand. Anyway pay attention, because if the chemistry is resin based, is difficult to clean and the residuals may be hygroscopic. So, I only can suggest you to read the data sheet and follow the instructions by the solder
Electronics Forum | Tue Feb 23 16:45:36 EST 2010 | dyoungquist
Davef is right on as usual. We are doing exactly what you do. Some smt with no clean paste then the plate through connectors on our selective solder machine using water soluble flux. We then clean with a ultrasonic water process. We do see the re
Electronics Forum | Fri Dec 01 16:02:33 EST 2000 | Jim M
Thanks for your reply. I 've tried to clarify and answer your questions. The water soluble paste used is WS3060, type 4. The boards are sent through a inline di cleaner after reflow. There is a hot Di waterwash, rinse and then hot air to dry the wa
Electronics Forum | Fri Dec 01 17:03:57 EST 2000 | Dave F
Curious, very curious ... Residues � Where are these residues? [solder & laminate / mask, solder only, laminate / mask only] What is the result of your analysis to the residues? How do you know it�s a flux residue, rather than a chemical by product
Electronics Forum | Thu Sep 20 01:13:05 EDT 2001 | Michael Konrad
Hi Dave, It may be. DI water alone will not build up residue. It can attack the finish of electro-polished (mirrored) stainless steel though. I have seen a white / chalky buildup on poly inline cleaners, usually isolated in the wash section. The
.gif)