Electronics Forum | Mon Mar 01 22:37:01 EST 1999 | Dave F
| Hello! SMT professionals, | | I do not know if anyone posted this question before. | Last week, I reflowed our newly designed thin Rigid-Flex pcb with 0.040" thickness. I found all of pins of a TQFP48 ic did not get wetted. I could see on the hee
Electronics Forum | Thu Feb 25 22:01:52 EST 1999 | Chris G.
| Read an earlier thread about using glass slugs to determine placement CPk. Can it actually be done this way? What's the procedure? Be interesting to know 'cause if it's feasible, I'd probably get myself a kit. None of us here are stat's experts
Electronics Forum | Fri Feb 19 00:32:40 EST 1999 | ZEEK
| We are using .040" diameter fiducials (global and local) on our boards. They are solder covered and HASL. I get batches of boards where the p&p vision system has trouble reading the fiducial. The fiducial looks dark on the screen. The board ven
Electronics Forum | Fri Jan 15 17:13:07 EST 1999 | Earl Moon
| | | | Hello, | | | | | | | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | | | | | | | So far, the tests I can think of
Electronics Forum | Thu Dec 24 13:43:30 EST 1998 | Earl Moon
| | | Anyone ever attach gold bump flip chip to FR4 or Alumina substrates. Am trying to find a solder which is acceptable for use on gold. Am worried about gold imbrittlement since the gold bumps on the flip chip are .004"x.004"x.001" solid gold. T
Electronics Forum | Thu Nov 19 11:06:40 EST 1998 | Earl Moon
| We have some PCB�s in our warehouse in Manaus - Brazil. They are stored for more than 2 years , in a condition of 25 degrees centigrades and a humidity ranging from 60% to 90%. | Do these conditions cause the PCB�s to deteriorate over time? If so ,
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Thu Aug 29 06:48:01 EDT 2002 | yngwie
I have seen several Imm Ag pad on the assembled board which have a copper colorleaching through the silver plating This happened on the pad which was not deposited with paste during the assembly process. Don't know if it is a problem, but we only
Electronics Forum | Mon Mar 04 17:52:59 EST 2002 | davef
Yes, providing the surface of the via is solderable. * If so, how much paste? => Vias come in various sizes. Boards vary in thickness. So, the amount of paste to fill a via varies. Roughly, you�ll need twice as much paste as the volume of the via
Electronics Forum | Fri May 03 18:10:17 EDT 2002 | stownsend
Okay, here goes another thread about gold plating. I have been using gold plated PCB's for about two years now, with mostly very good results. The main reason I started using gold in the first place was because it is flat, solder wets to it nicely,