Electronics Forum | Wed Nov 07 21:36:17 EST 2012 | davef
Multiple process and rework thermal cycles are brutal on boards and components. Improving reliability of products through reducing thermal stress ends-up being a major driver to the interest in lower MP LF solders. Binary LF solders require the addit
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Tue Feb 17 04:52:13 EST 2004 | John W
There's normally a number of reasons people want to know what melts 1st, 1 - to see if you know, 2 voiding issues - whole can of worms 3 device alignment. One of our collegues has said that most balls are Eutectic, that's in fact not totally correct.
Electronics Forum | Wed Jul 07 13:56:57 EDT 2004 | Pierre RICHARD
As converting our boards to lead-free finish (Immersion White Tin) we decided to change de mask color from green to blue. We thought this would be a good idea to spread the idea so we could easily recognize the type of solder application related to t
Electronics Forum | Wed Dec 24 15:28:17 EST 2008 | edmentzer
We use SN100C for wave soldering and hand Lead free soldering and have had very good results. The wire cored solder for hand soldering flows good and makes very good solder joints. The SN100C in the wave solder machine also works very good. We use
Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Sat Nov 03 10:57:27 EDT 2012 | davef
EricR: Regarding "*** By the way, since we have used the Tin-Silver-Copper lead free solder there has been a strange liquid type chemical leek from the oven exhausted pipes." ... I don't know anything about your process, but the first thing I'd inve
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Wed Apr 06 08:27:12 EDT 2011 | kaschliman
Our two component suppliers use 99.5Sn/0.5Cu and 97Sn/3Ag solder (respectively) for tinning their leads. We use 98.9Sn/.66Cu/.33Ag solder in our wave solder machine. Is there any significant advantage to either tinning process regarding solderabili