Electronics Forum | Mon May 06 00:09:00 EDT 2002 | ianchan
as a followup thought, what is your current peak reflow deg-C? and reflow timing (sec)? Au/Ni calls for reflow temperature of 217 deg-C for solder fusion that produces secondary eutectic alloy. there was one time we thought 183 deg-C was the magic
Electronics Forum | Fri Oct 31 13:06:42 EST 2003 | Kris
Hi, What would also be important is the time above 217. 20 secs above 225 may be the same as 45 secs above 218 That 7 degres might just buy you enough to sweep the non lead free components through Has anyone tried 220 or 218 peak temp but at lo
Electronics Forum | Wed Jan 05 15:54:51 EST 2005 | Frank R.
Hi, Now in my wave the PCB TOP Side temperature before WAVE is 110 - 115 DegC and the Peak temp in the wave is 240 - 245. These informations are for an 63/37 Alloy. What is the PCB TOP Side temperature and the peak temperature for Lead Free Wave Sn
Electronics Forum | Mon Oct 10 20:06:59 EDT 2005 | nuezmaster
Does anyone have any experience running Aluminum Electrolytic Caps with a SAC305 alloy. The profile for the solder calls out a peak temp of 235-255C and 60-75 seconds above 217C. Most can cap manufacturers are calling out for 230-245c max for no lo
Electronics Forum | Wed Dec 07 14:56:35 EST 2005 | rhorowitz
Dear Mr Duckman, I am a Regional Sales Manager with MIRTEC. I would be happy to discuss your application with you. If I can be of any assistance, please feel free to call or e-mail me at your convenience. Respectfully, Robert Horowitz 203-881-5559
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Thu May 25 08:58:14 EDT 2006 | inds
aj, check out the link http://www.smtnet.com/forums/index.cfm?fuseaction=view_thread&CFapp=8&Thread_id=10387&mc=5 as Samir mentioned in that link, try keeping your peak temp within 220-225degC.. TAL 217 around 20-40 sec..depending on your ball d
Electronics Forum | Mon Feb 12 13:58:10 EST 2007 | campos
Tks for the answers,, My concern is about the intermetalic layer,,I run SMQ230 LEAD FREE paste.. its liquidous at 217C..the oven have 7 zone, but I run in 5 zones also with a more agressive profile (due to the line rate)..I would like to know if runn
Electronics Forum | Tue Feb 13 15:20:12 EST 2007 | billyd
Fellas: I'm having a tough time with voiding with my lead free water soluble paste under my large BGAs. I know some is almost inevitable, but this is more than I'd like. This is with a slope of .9, soak of 60 seconds, above 217 for 85 seco
Electronics Forum | Thu May 03 22:41:36 EDT 2007 | davef
How do the SUBJECT "CCLEF100X8M-R" and the link on your posting relate to each other? Assuming the link is important, [couldn't you find an English site posting your component?] Look here: http://www.calmicro.com/applications/app_docs/ap-217.pdf