Electronics Forum | Wed Nov 03 09:42:31 EST 2004 | dramos1
Hi Simon, Thanks for the immediate reply. We really appreciate it very much. Currently, we are using Class 2 for the visual inspection criteria of our telecom boards. In IPC-A-610 Rev. C criteria, there are TARGET, ACCEPTABLE and REJECT criterias.
Electronics Forum | Thu Apr 14 09:39:41 EDT 2011 | blnorman
ROSE has the advantage in that it does have a specific acceptance criteria (J-STD-001), whereas the IC does not. ROSE allows the test to be run at ambient or at an elevated temp, IC requires the component/board/assembly to be "cooked" for 1 hour @ 8
Electronics Forum | Wed Nov 28 12:33:01 EST 2001 | tonkowa
Did you have any luck in finding an acceptance criteria that QA accepted? We have had excellent results on signal pins of D-sunb connectors but the grounding prongs dod not meet IPC standard 610C, 4.3 Thanks, John
Electronics Forum | Mon Feb 25 14:32:37 EST 2002 | Kelvin
We always talk about the halide free fluxes and solder pastes. Is there anyone tell me what is the industrial acceptable level of halide content or contamination in flux residue? All comment are welcome !!! Kelvin
Electronics Forum | Fri Sep 13 13:16:55 EDT 2002 | stepheno
Moisture will still seep in over 12 years. Moisture barier bags are not 100%. If you accept them, conditionally accept them, and don't pay for them untill you are happy with them.
Electronics Forum | Thu Apr 17 16:41:37 EDT 2003 | davef
60% ||||36% of ball area|| >36% ||Class2|| Accept|| Reject ||||45% of ball diameter|| >45% ||||20.25% of ball area|| >20.25% ||Class3|| Accept|| Reject ||||30% of ball diameter|| >30% ||||09% of ball area|| >09%
Electronics Forum | Wed Sep 15 06:53:48 EDT 2004 | John
Hi Everybody, Can enybody tell me what is acceptable level of defects for Wave soldering?I know that it's depends of many factors,but I want to benchmark my process. Thank you
Electronics Forum | Wed Nov 03 09:07:07 EST 2004 | dramos1
Hi, We would like to know on the IPC-A-610 rev. C standard for acceptable and reject criteria, do we have to satisfy all that are listed on the manual or either one will be OK? Thanks for all the assistance that will provided. Dennis1
Electronics Forum | Wed Nov 03 09:59:47 EST 2004 | Simon UK
Hi Dennis, I would say that you must meet one of the acceptable critera if you have others list, but it depends. Do you have a specific query in relation to a solder joint or other defect?? Simon UK
Electronics Forum | Wed Nov 03 15:55:42 EST 2004 | davef
Dennis: The IPC-A-610 requirements are seperate. * You need to meet all acceptance requirements, in order to be in compliance. * If you reject a part for any reason, you are not in compliance.