Electronics Forum | Thu Apr 21 11:43:03 EDT 2005 | davef
We understand the problem of trying to coat over RTV. We have seen the same problem with acrylic and urethane coatings not wanting to stick to RTV. Some acrylics seem to be worse than urethane. Since this is a new product, may be you could pot your
Electronics Forum | Mon Jan 03 00:30:30 EST 2011 | raghu
Contact your distributor for the coating or > Humiseal directly. Humiseal has had a recent > issue with batches of 1B31. The specific problem > is lack of adhesion, which is what you have as > well. You need to find out if your batch # is one >
Electronics Forum | Wed Dec 22 02:49:37 EST 2010 | raghu
Dear Sir, Please clarify my doubt... What will happened if acrylic conformal coating is mixed with poly urathane conformal coating and mixing of this composition is used to apply for electronic PCBs Thanks & Regards, Raghuveer S.
Electronics Forum | Thu Sep 08 17:31:09 EDT 2005 | davef
Urethane CC have greater resistance to solvents than acrylic CC
Electronics Forum | Sun Dec 26 23:33:38 EST 2010 | raghu
Thanks for your reply sir, We have done production with Machine application earlier, of control electronics sub- assys of some boards with acrylic conformal coating by using one tank... And some boards with polyurathan conformal caoting by usin
Electronics Forum | Wed Jul 29 11:28:54 EDT 2015 | pankyb1261
How many times does it have to flex. There are acrylic conformal coatings that can be bent once to 90 degrees or so
Electronics Forum | Wed Oct 17 02:04:39 EDT 2018 | robl
SCC3 has an operating temperature of 200C, as long as it is heat cured at 100C. https://www.electrolube.com/pdf/tds/044/DCA.pdf It's also a silicone so needs to be coated & cured away from anything you value. Otherwise there are plenty of PU's and
Electronics Forum | Wed Dec 22 04:40:37 EST 2010 | sachu_70
Any specific reason to consider such situation?
Electronics Forum | Fri Jan 22 14:31:14 EST 1999 | Dave F
| I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the c
Electronics Forum | Fri Dec 18 09:07:24 EST 2009 | tommyg_fla
dave, where I work they are having the same problems with 1B31 acrylic. The coating thickness is 6-8 mils dried so that have to do several passes with an air dry between them and a final oven cure. They think that it might be related to the heating r