Electronics Forum | Fri Jun 01 09:50:01 EDT 2001 | lumidor
Our PCBs manufactured with no clean flux have a waxy film on the board...is this normal? Our contract manufacturer recently switched to no clean from water wash. Thanks Carl
Electronics Forum | Thu Sep 17 08:23:03 EDT 1998 | Wayne Carlson
I need an evaluation process to prove to a customer that our no-clean process does not leave excessive residue? Any ideas?
Electronics Forum | Tue Sep 10 22:29:01 EDT 2002 | scottefiske
Many times after initially cleaning in the solvents recommended by the paste/material manufacturer, a light white haze may still be visable...try using a soft bristle brush to remove the remaining residues. By this time the residues that remain will
Electronics Forum | Wed Dec 08 08:38:46 EST 2004 | davef
KS: You're correct. The standoff on a 1.00mm and 1.25mm BGA is high enough to allow cleaning. The standoff on 0.8mm BGA does not allow proper cleaning, even with saponifiers.
Electronics Forum | Mon Dec 13 16:25:37 EST 2004 | saragorcos
Hi Scott - No clean assemblies have a very low tolerance for processing residues, and long term reliability is compromised if residues from incoming bare boards, components, or un-solublized flux residues are not dealt with. It is critical to contro
Electronics Forum | Tue Aug 10 03:13:30 EDT 1999 | Dreamsniper
| hello to everybody, | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | does anybody know how to eliminate flux residues or how not to produce them during rework operatio
Electronics Forum | Mon Oct 22 11:47:59 EDT 2007 | brulal1
Thank you guys for your help, I do not clean any on my assemblies who are build by the SMT an wave soldering department, we do used liquid fluxes Kester 951 and cored wire keester 245, usually it�s for batteries connector, led, terminal and wire rap
Electronics Forum | Tue Mar 07 21:19:50 EST 2000 | Van Hoang Dinh
I have few problems below, 1.I had problem with clean glue stencil at the midle of the process and after the process. 2.Very hard to Fix the bridging on the (close pin) connectors through the wave. Anyone can help on this. Thanks Van
Electronics Forum | Tue Mar 07 21:19:50 EST 2000 | Van Hoang Dinh
I have few problems below, 1.I had problem with clean glue stencil at the midle of the process and after the process. 2.Very hard to Fix the bridging on the (close pin) connectors through the wave. Anyone can help on this. Thanks Van
Electronics Forum | Mon Aug 09 10:10:29 EDT 1999 | Gian.D
hello to everybody, we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; does anybody know how to eliminate flux residues or how not to produce them during rework operations? Th