Electronics Forum | Thu May 30 10:31:03 EDT 2002 | robbied
Hi Yannick. This is an issue that we are just recently getting into but here is some ifo that I have gathered so far. I have seen/ used 2 different rework machines. The one we have bought is a 'PACE TF2000' which was at the lower cost end of the mar
Electronics Forum | Thu Sep 19 11:14:45 EDT 2002 | Jim M.
We had lots of problems with bridging on 15.8mm pitch, QFP17-160 at the start.The board was .032 thick, double sided-six boards to a panel. Here is the problems (not neccessarily in the biggest to little but as i remember them) and solutions that he
Electronics Forum | Mon Mar 29 12:10:14 EDT 2010 | rway
Test Jet will work for catching lifted leads, certainly. X-ray is the only thing for testing for internal solder defects such as voids and cracks. I personally do not have any experience using X-ray, so I cannot advise on its reliability. Perhaps
Electronics Forum | Mon Mar 13 15:35:56 EST 2006 | russ
You're a piece of work! Why don't you work for any of the major wave companies? So how does slowing the conveyor speed eliminate drying flux? And when you slow it down, what speeds it up to make you say "I lower the wave because I get shorts going
Electronics Forum | Fri Mar 26 11:31:34 EDT 2010 | rway
I have been using ICT for a number of years. It is still a viable resource for catching defects in the production process. AOI doesn't catch everything, such as bridging on QFN or J-lead devices (this will depend on the type of AOI and camera syste
Electronics Forum | Tue Nov 29 14:55:17 EST 2011 | jlawson
N2 is a reflow process widener so to speak, for leaded reflow less of a impact, for LF more impact, and if using finer LF solder pastes T4,T5 and smaller paste deposits generally, it helps widen window for flux in paste in oxide protection during soa
Electronics Forum | Sat Jul 24 00:04:55 EDT 1999 | Scott McKee
| | | There is a practise within the industry of an Inspector inspecting a board, and that same Inspector performing touch-up. My opinion is that the Inspection and Touch-up operations should be separate functions whereby the Inspector is not perform
Electronics Forum | Mon Jan 10 18:35:05 EST 2011 | eadthem
Ive used a Mirtec machine for 3 years MV3L with side angle inspection. Mirtec has some issues documentation, and repair plus. But there machine is impressive and the AOI software is good. We can find about 90-99.99% of all errors using just the 5
Electronics Forum | Mon Jun 08 14:19:30 EDT 1998 | Gary Simbulan
Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have
Electronics Forum | Wed Jul 19 12:54:04 EDT 2023 | calebcsmt
Since side fillets are not a requirement for QFNs/BTCs due to some packages not having wettable side terminations, how does one determine if the side terminations are actually solderable/designed for wetting? Is it simply if the side terminations