Electronics Forum | Fri Jun 04 17:47:34 EDT 2021 | pjchonis
Thank you very much for your insights! I appreciate your time.
Electronics Forum | Fri Jun 04 14:35:39 EDT 2021 | pjchonis
Hello everyone, I am just curious if anyone has any common problems when using Kyzen or Zestron? Why did you initially choose to use one of their products in the first place? In your opinion, what are the pros and cons? I would love to know your tho
Electronics Forum | Fri Mar 19 12:17:15 EDT 2010 | stepheniii
Be carefull if you go to no clean. Or be prepared from complaints from the test department regarding their ICT pins getting dirty.
Electronics Forum | Wed Mar 04 14:35:16 EST 2009 | clampron
Good Afternoon Everyone, I have a customer who is inquiring as to the use of a no clean solder paste on their RoHS assembly. We are currently building this with OA, cleaning and then underfilling the QFN, BGA comonents after a sucessful ICT. Does any
Electronics Forum | Mon Feb 19 11:25:07 EST 2001 | markt
I am currently cleaning solder paste and adhesive stencils and misprinted substrates manually by using IPA, chem wipes, Q-tips, etc. Can you recommend a machine and chemistry that will clean all these applications?
Electronics Forum | Mon Dec 18 13:00:47 EST 2006 | grantp
Hi, We have a white residue, which is visible, and we would like to have the produce clean as it's a PCI card, so users see the PCB. I am wondering if we need to install a cleaning stage to the line for these kinds of products. Can anyone give som
Electronics Forum | Mon Dec 18 14:36:09 EST 2006 | samir
Yikes!! In-line cleaning, to clean cosmetic and benign residues (from a NO-CLEAN) flux... You sure you can't switch fluxes? Another variable with residues is the solder mask. Depending on mask type (glossy, matte, semi-gloss, or semi-matte), will
Electronics Forum | Mon Dec 18 23:24:50 EST 2006 | grantp
Hi, Yes, I would hate to resort to cleaning, but the product must be clean. We have been using palettes to keep most of the flux off the PCB, but there is still residue around the connectors. Does anyone suggest a good no clean flux to use with le
Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano