Electronics Forum | Fri Sep 04 02:09:03 EDT 2009 | sachu_70
Hi Walter, Do you refer to a sprayfluxer operation? The problem seems to be a parameter setting issue. 1. Ensure the wide angle spray reaches PCB with optimum jet pressure. You could pass a glass plate to understand flux coverage and view Jet pressur
Electronics Forum | Mon Jan 08 10:29:15 EST 2007 | jaime39
The water soluble flux residue is staying there because the rinsing temperature it may be too low. The flux needs about 130-140 degrees celcius to become soft. If you are using water soluble flux, as per IPC A 610 standards it needs to be remove comp
Electronics Forum | Sun Dec 11 22:39:36 EST 2016 | ppcbs
We have been using the Amtech line for over 12 years now with all of our PCB and BGA Rework. The NWS-4400 is mildly active and will give better results with Lead Free Solder. Note that the LF-4300 is considered a No-Clean. However it will show lea
Electronics Forum | Wed Apr 28 14:52:03 EDT 2010 | davef
When we hear the words 'flexible circuit' and 'delamination' in the same sentence, we think: * Excessive reflow temperature. * Entrapped moisture. Boardhouse: I hope this is a step towards redemption.
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Thu Aug 20 14:52:40 EDT 2009 | davef
Armando: We're guessing that the white residue is on the laminate also. We believe that the residue has something to do with your low residue flux and water. It could be: * Water contamination in the flux. * Poor selection of preheat temperature that
Electronics Forum | Tue Aug 22 10:53:45 EDT 2000 | Dr. Ning-Cheng Lee
Excellent question. Alloy development is relatively easy compared to flux formulation. New fluxes for Pb-Free alloys need upgrades in 2 critical areas: 1) thermal stability 2) oxygen barrier efficiency Since the Pb-Free alloys require reflow proce
Electronics Forum | Fri Dec 16 10:25:37 EST 2005 | solderiron
Rather than cleaning a water soluble flux residue off the board, by encapsulating the product. covering the board or the component with lets say a Hysol encasulant. Would this prevent the active flux residue from migrating and deteriorating the elect
Electronics Forum | Thu Jul 07 17:08:28 EDT 2005 | Inds
how fast are you ramping your profile..and how long are you soaking it.. are you giving enough time for the flux to get activated...
Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use