Electronics Forum | Thu Sep 02 07:50:27 EDT 2010 | sachu_70
Just to add to my comments,solder joint voids do occur in LGA. Voids in LGA can be larger due to geometry and greater ratio of flux to solder. IPC-A-610D specifies a greater than 25% voided area is a defect for BGA, however, it does not specify the d
Electronics Forum | Wed May 27 13:50:38 EDT 2015 | ingallsd
I saw a question regarding the acceptability of stacking chip components at this forum posted in 2000. Unfortunately no one could cite any applicable IPC sections at that time. I am now able to find that this is acceptable per IPC-A-610D, Section 8.
Electronics Forum | Fri May 11 07:37:22 EDT 2007 | davef
IPC-A-610D 3 Handling Electronic Assemblies 3-1 3.1 EOS/ESD Prevention 3-2 3.1.1 Electrical Overstress (EOS) 3-3 3.1.2 Electrostatic Discharge (ESD) 3-4 3.1.3 Warning Labels 3-5 3.1.4 Protective Materials 3-6 3.2 EOS/ESD Safe Workstation/EPA 3-7 3.3
Electronics Forum | Thu Mar 03 16:41:11 EST 2005 | davef
According to an on-line posting ... SMTA On-line Presentation Comparing Industry Standard Revisions March 9: IPC-A-610 with Regards to Lead-free Technology There have been extensive and significant changes to the industry standard IPC-A-610 with th
Electronics Forum | Fri Jul 08 16:35:04 EDT 2005 | Jason Fullerton
"Whether or not you need a toe fillet depends on your application. We have high reliability products where we can't use a QFN over a certain size, regardless of toe fillet. We have other applications where we meet the thermal cycle requirements for a
Electronics Forum | Fri Nov 13 08:27:43 EST 2009 | herman
Your customer is very unreasonable to demand void-free BGA SJs. Minor voiding is not a condition for rejection per IPC-A-610D, J-STD-001D, or even J-STD-001DS (Space addendum). Having said that, let me tell you that the voiding has little or nothing
Electronics Forum | Thu Mar 23 22:26:53 EST 2006 | Joseph
Dear all, Referring comment from Mr. Jack,IPC director certification & assembly technology, the term "fillet tearing" is too broad. Cracks or fractures in the required fillet area, with SnPb or LF alloy and whether you call it tearing or not, is a D
Electronics Forum | Tue Dec 04 08:34:07 EST 2007 | davef
We no advice to give you on the topic, but maybe while you're waiting for others to reply, reading a trade journal article on the topic might help. Below is a link to "Pin-in-hole reflow (PIHR) and lead-free solder joints" by David Bernard, Bob Willi