Electronics Forum | Thu Nov 19 05:18:37 EST 2009 | prodivegsr
Hi All, Recently we are working on the conformal coating process using Humiseal chemical 1B73 and thinner 521. Bubbles on component body/joints are seen after gone through the IR Reflow Oven. During the conformal coating, only tiny bubbles seen af
Electronics Forum | Wed Dec 02 10:14:42 EST 2009 | duso02
As a large coating house we use 1B73 daily and we have very few issues with bubbles. We very rarely bake it as the air cure is so short. Also, we only use thinner 73 vice 521. Another question would be; how is it being applied? How thick are you appl
Electronics Forum | Mon Nov 30 09:05:47 EST 2009 | sforman1
totally wrong. a. I do not reccomend Humiseal UV products. My Dad started Humiseal. b. As the former VP of Dymax Corporation I know quite a bit about this subject. Contact Dymax in Torrington, CT and inquire about 984LV. c. You will definetly sleep b
Electronics Forum | Wed Dec 02 00:31:37 EST 2009 | jlawson
UV40 for you info was developed in Humiseal EU and has been tested heavily against Dymax product. UV40 is a great product has many approvals from major auto and whitegoods makers.... I have seen comparisons UV40 to Dymax 984LV and Dymax comes out se
Electronics Forum | Wed Dec 02 20:11:37 EST 2009 | prodivegsr
Hi Lou, we are using a fluid dispensing machine. our current requirement is around 50um. From the Datasheet,the thinner 73 has a higher evaporation rate of 1.0 comapring with thinner 521 at 0.6... does the higher evaporation rate eliminate the bu
Electronics Forum | Tue Jan 30 20:38:32 EST 2007 | davef
NASA Internal Advisory: NASA-Issued Return to Flight Wristbands Contaminated with Silicone [snip] 10. PROBLEM DESCRIPTION: Recently we have been made aware of a silicone problem associated with the "Return to Flight" wristbands. These wristbands are
Electronics Forum | Wed Jun 03 15:22:12 EDT 1998 | Greg Curler
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Sat Oct 08 11:57:58 EDT 2016 | davef
A friend in the contract coating business said: "... ask why the wire is [teflon] coated in the first place, as only the solder joints should be coated in this situation as the flexing/bending of the wires will cause the coating to crack and flake of
Electronics Forum | Thu Aug 20 07:11:25 EDT 2020 | sssamw
What your said looks like a acrylic coating thermal expansion causes small solder joint crack. Do you cure coating with heating, or heating after curing? Solder joint crack while you see resistor and QFN trouble? Clear and detail description of your
Electronics Forum | Mon Mar 08 11:54:06 EST 2004 | Wayne Smith
Currently experiencing a problem where the plastic molded bodies of tantalum capacitors are cracking during my SMT processing. Caught after our conformal coating process. I don't know where in the process they cracked. Currently running an exper
.gif)