Electronics Forum | Mon Mar 20 13:56:04 EDT 2017 | pjc
Kleenox is designed for cleaning and protecting the solder bath in wave solder pots from air oxidation and formation. Kleenox is formulated to remove oxides. Kleenox can be used with tin/lead and lead-free solder. http://www.americancleanstat.com/k
Electronics Forum | Wed Aug 26 22:00:42 EDT 1998 | Dave F
| What approach do you you use to reducing wave solder dross? What is your experience with Klennox? | Dave F Klennox should be spelled Kleenox. Dave F
Electronics Forum | Tue Dec 30 17:11:51 EST 2003 | davef
Just a moment of 'hair-splitting', Klennox does NOT reduce the amount of dross, it reduces the amount of solder in the dross. Look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=3836
Electronics Forum | Thu Aug 27 12:28:02 EDT 1998 | Ryan Jennens
| | What approach do you you use to reducing wave solder dross? What is your experience with Klennox? | | Dave F | Klennox should be spelled Kleenox. Dave F Kleenox works well for removing accumulated dross as it separates the dross from the solde
Electronics Forum | Mon May 23 10:53:32 EDT 2005 | HOSS
Eric, We also have a UPK 650C. Our machine was configured for N2 and using the ConTour nozzle. If you're using this nozzle without N2 you're creating tons of dross unnecessarily not to mention probably getting tons of icicling. We found out the h
Electronics Forum | Fri Aug 28 13:20:45 EDT 1998 | Justin Medernach
| What approach do you you use to reducing wave solder dross? What is your experience with Klennox? | Dave F Dave, I use Kleenox on my Air-Vac Volcanic Soldering pots. The stuff works great. It significantly reduces the amount of dross you remove
Electronics Forum | Fri Aug 28 13:23:49 EDT 1998 | Chrys
| | | What approach do you you use to reducing wave solder dross? What is your experience with Klennox? | | | Dave F | | Klennox should be spelled Kleenox. Dave F | Kleenox works well for removing accumulated dross as it separates the dross from t
Electronics Forum | Sat May 21 08:22:42 EDT 2005 | davef
We agree with the previous poster. 50 pounds sounds like a lot. We don't know: * How often you dedross? * What method you use for dedrossing? * What portion of your dross that is dross versus solder? * How many boards do you run between drossings?
Electronics Forum | Sat Dec 02 11:35:30 EST 2006 | davef
Best dross remover is to not produce dross. Search the fine SMYnet Archives for previous discussions Dross will not increase signicantly * Another story, that lead-free solders will generate a greater volume of dross than conventional materials, is
Electronics Forum | Wed Oct 04 13:06:21 EDT 2006 | greg york
Sorry Bert For some reason I'm not getting the Email notifications so appologies never saw the reply. The mettalic antidrossing agent reduces the dross to levels of est. 50% less than compared to 63/37 alloy. When used with SACP/0307 alloy and SACP/