Electronics Forum | Tue Oct 21 23:28:59 EDT 2003 | xz xiao
We all know the Lead Free process is trend, so we trial run it, now it is only my comment that we have a good achievement after several tries,we have taken serveral photos about Lead Free process with ErsaScope. 1.The surface of the solder joint are
Electronics Forum | Tue Oct 21 23:29:08 EDT 2003 | xz xiao
We all know the Lead Free process is trend, so we trial run it, now it is only my comment that we have a good achievement after several tries,we have taken serveral photos about Lead Free process with ErsaScope. 1.The surface of the solder joint are
Electronics Forum | Fri Jul 27 10:07:18 EDT 2007 | rgduval
Our preference has been ENIG. We find that we achieve higher quality (visually) soldering for through hole and surface mount parts, with less handling issues than when we use white-tin, or immersion tin. We are about to do a test on some boards tha
Electronics Forum | Thu Jan 29 11:30:56 EST 2009 | rgduval
As others have said, you'll have some difficulties getting good reflow on pb-free out of a 3-zone oven. We did it with a 4-zone for awhile, but only had really good success on low thermal density boards. That said, you should definitely check your
Electronics Forum | Wed Jan 07 12:09:40 EST 2004 | Kris
Hi All, Does any body have any information on hot bar lead free soldering ? Need papers or experimental data ASAP Thanks
Electronics Forum | Sat Oct 18 09:30:43 EDT 2008 | hussman
Sounds like a part problem. You can SOMETIMES over come this with a hotter profile. We see this a lot with brokered parts. Seems like a lot of people are rejecting parts because a lot of companies haven't perfected their RoHS process, yet produce
Electronics Forum | Fri Oct 24 13:21:12 EDT 2008 | evtimov
Hello Bong, I would make one test only. Make one batch using the problem part from a different vendor. That will answer your main question. For me the part is causing all your problems. If it is possible, change it. Last time having problem like you
Electronics Forum | Fri Oct 17 22:36:35 EDT 2008 | arosario
Hi All, We just started build a new product and I am encountering many non-wet rejects in our new product. I need help on what should I look into to improve our Yield. Please see below back ground 1. We are using DEK Infinity as printer. 2. We are mo
Electronics Forum | Sat Oct 18 20:35:25 EDT 2008 | arosario
I see, maybe changing my peak temp in reflow will help. I'll try do eval again... Actually, once I did have evaluated a longer pre-heat but on my previous eval, I didn't change the peak temp. Maybe reflow can help compensate to my problem in the part
Electronics Forum | Wed Apr 26 07:37:34 EDT 2006 | amol_kane
"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from