No we have a battery spring that is soldered directly to a PCB (standard tin plated copper PCB). The Battery spring supplier (and I have no confirmation he makes them or buys them) claims they are tin plated. When trying to solder to them it is very
Electronics Forum | Fri Apr 25 14:49:34 EDT 2014 | isd_jwendell
If the tab is Sn plated, you can solder to it as long as your iron has enough power (watts). If you continue to have trouble then it probably isn't Sn plated.
Electronics Forum | Tue Apr 22 08:55:54 EDT 2014 | davef
I assume that you're talking about wanting to solder to metal tabs that are spot welded to the battery terminal. These tabs are not meant to be soldered. The metal was special selected for welding. In the old days, you could buy plumbing flux at th
Electronics Forum | Thu Jun 15 18:15:34 EDT 2006 | nickel
If you have time, download the free Practical Guide to Understanding the Scope of the WEEE and RoHS, you will find what they say about UPS. They consider UPS out from the field of application of RoHS. ORGALIME (Bruxelles)is the European Engineering
Electronics Forum | Thu May 25 16:05:08 EDT 2006 | nickel
ERA is well paid by EC to add further confusion !!! Requiem
Electronics Forum | Wed Apr 21 17:08:32 EDT 2004 | dave
Congratulations on your new customer. This could be a keeper. Here's what you're familiar with: Electroless Nickel - per MIL-C-26074 and ASTM-B733. Electroless nickel describes the plating of nickel deposits, which may contain phosphorus and boro
Electronics Forum | Tue Feb 22 09:01:50 EST 2005 | davef
It could be that you're starting with hyper corroded nickel, before you even begin work. With electroless nickel, everybody looks at the nickel, but the cause turns out to be the immersion gold is too aggressive [during fabrication]. Immersion gold
Electronics Forum | Fri Aug 17 11:55:31 EDT 2001 | davef
5uin. Your nickel thickness is fine. Although if you wanted to trade costs, consider giving-up nickel to 150uin thickness, while increasing the gold thickness. Gold over electroless nickel creates brittle joints because of phosphorous in the nicke
Electronics Forum | Mon Feb 14 12:19:32 EST 2000 | Dave F
Dean: I associate black plague as an immersion gold process problem (although I could easily be wrong): Everybody looks at the nickel, but the cause turns out to be the immersion gold is too aggressive. The immersion gold works by corroding the nic
Electronics Forum | Thu Jan 03 17:39:34 EST 2008 | flipit
Why are you using stainless steel? Corrosion resistance? Can the stainless be gold plated? I think this can occur metallurgically. Maybe nickel first then gold. Why are you removing the nickel? Nickel is somewhat magnetic. Had an application onc