Electronics Forum | Thu Oct 04 13:34:02 EDT 2007 | rgduval
I'd be happy to tell my customers that they need to provide more parts...the problem is, we specialize in short runs. So, if the customer pinches pennies, and only buys 50 pieces for 50 piece demand, I need to be able to deal with it. Hence, the
Electronics Forum | Thu Jul 23 18:32:02 EDT 2009 | fleesmtchoi
i see one company saying lewis clark company advertise win frost and sullivan award. but i find frost and sullivan award is not good award and cannot be trusted. document i find internet. http://ipvideomarket.info/report/should_you_trust_frost_&_
Electronics Forum | Tue Sep 17 15:40:59 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Tue Sep 17 15:47:04 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Thu May 26 00:42:19 EDT 2005 | nicholas2005
Ok, I just need someone to give me some feed back on a few questions I have. If anyone could help me that would be great. Example: take a Fuji CP-4 feeder for instance! If I machine my own, place my own parts on it, and place my own company name, and
Electronics Forum | Fri Jul 15 03:29:52 EDT 2005 | dougs
thomas, why isn't it process control, you cant just think that because you've set up your machine properly ( pot temp, wave height, pre-heat etc etc )that everything is going to be ok, there are other factors that you wont find with wave riders or
Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
Electronics Forum | Wed Jun 06 09:28:35 EDT 2007 | larryp
Thanks for the help but I do have another question. First I guess that just the touching of the smock to the skin is anough to give the charge on the person a path to the smock. OK I can accept that if button up at the breast and sleeves. Now I kno
Electronics Forum | Tue Oct 18 10:36:46 EDT 2022 | winston_one
Dear proffessionals! Question is about this alloys - Sn99Cu07 and Sn100 (Sn100C,Sn100Ni+ etc.). Is it O'k to mix them? In my case to use Sn99Cu07 as addition to selective soldering machine bath with Sn100C? Main components are the same, but minor add
Electronics Forum | Thu Jun 15 18:15:34 EDT 2006 | nickel
If you have time, download the free Practical Guide to Understanding the Scope of the WEEE and RoHS, you will find what they say about UPS. They consider UPS out from the field of application of RoHS. ORGALIME (Bruxelles)is the European Engineering
Reflow ovens for automated SMT PCB assembly, specializing in lead free processing and nitrogen reflow. The best convection reflow ovens on the market.
4 Vreeland Rd.
Florham Park, NJ USA
Phone: 973-377-6800