Electronics Forum | Mon Jan 24 20:59:34 EST 2005 | davef
What is your specific problem when soldering polyimide [amide]?
Electronics Forum | Wed Dec 03 08:39:09 EST 2008 | sys_steven
boards are polyimide, and it is an ipa rinse with the solvent cleaner.
Electronics Forum | Tue May 12 22:57:30 EDT 2009 | davef
Polyimide bare board with tin over nickel solderability protection.
Electronics Forum | Wed Apr 21 03:10:37 EDT 1999 | Richard Cooper
To all who will be potentially my salvation, I am currently researching Polyimide stencils for possible use and manufacture. If I may be indulged - with due reference to all past enquiries and notes on the subject - can anyone offer an up to date op
Electronics Forum | Mon Oct 04 20:06:31 EDT 2004 | davef
We know SIR coupons are not ROSE coupons, but coupon boards are: * IPC-B-24 (copper and HASL, FR-4 and polyimide) * IPC-B-36 (bare copper and HASL, FR-4 and polyimide) * IPC Phoenix board (bare copper, FR-4) * IPC-B-25A (FR-4, bare copper only)
Electronics Forum | Wed Oct 30 10:35:23 EDT 2013 | vleasher
I was looking for thick polyimide discs that are usually applied by a connector manufacturer for a pick surface. Every disc I have found online is .001 thick unlike the more rigid ones. We are hoping to find a source so we can manually apply to some
Electronics Forum | Sun Apr 05 09:46:47 EDT 1998 | Earl Moon
| We are looking at reflow soldering some Flexi-rigid | pcbs. I have heard that IR reflow soldering can make the Polyimide "self heat" and cause de-lamination. | Does anyone have any info. The thermal problems associated with polyimide rigid/flex de
Electronics Forum | Wed Jun 02 09:50:00 EDT 1999 | Earl Moon
| Hello all | I have a question concerning whether or not there is any special requirements to follow for assembly of a Polyimide PCB card. The customer has the following information on there documentation but since we have never built anything with
Electronics Forum | Wed Jun 02 09:55:31 EDT 1999 | Jason Gregory
Hello Dan, I have recently started using polyimide, but not for the standard uses. I designed a pallet for holding small, thin (about .0018" thick) RF boards that were being reflowed inside their aluminum housings. They were screwed down to prevent w
Electronics Forum | Tue Sep 21 15:31:05 EDT 1999 | Hugh Martin
| | | | I like to see if anyone has any info or experinces with metal inspection templates in a post oven process. | | | | My problem issue is the ESD, since they are metal(12 mil stencil material). I welcome any comment. | | | | | | | | Thank you.