Electronics Forum | Tue Oct 07 12:35:10 EDT 2008 | andy_pal
Hi All, I am using COB on my DOUBLE SIDED PCB. lastly we used Eletrolytic Ni / Flash Gold Plating. Our Boards vias Failed the UL corrosion Test. we did some cross-section analysis and found 10.75 �m of Nickel and 0.022 um of Gold and as the Process
Electronics Forum | Mon Jul 30 12:45:00 EDT 2018 | mdkmdr
Trying to get a sense of the push-pull going on between designers and manufacturers on the subject of 'one test point per net'. Getting a feeling like the new paradigm is doing all of the electrical tests as functional at EOL and relying almost comp
Electronics Forum | Mon Feb 23 13:25:21 EST 1998 | Steve Gregory
Steve - you must not work to IPC class 2 or 3 requirements. If the solder is "pillowed" around the lead, I would strongly suspect a wetting problem. Most of the Paladium leads I see soldered have a strong line of demarcation but no pillowing. Hav
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Tue Apr 11 16:42:56 EDT 2000 | Chad Notebaert
I�m thinking �Poor intermatallic� It could be a few things. Lets start at the beginning. -Is your paste a 63/37 mixture? -Have you monitored you screen printing, Verify Solder deposition, Are you getting enough paste? -You say the solder looks like i
Electronics Forum | Wed Feb 25 01:24:34 EST 1998 | Steve Gregory
Dave, I confess I was a tad too general and a bit too extreme describing the way ALL solder joints look on palladium coated leads. I should been more specific about the "pillow-effect". I've seen it regularly with palladium coated leads on small SOT
Electronics Forum | Tue Jan 31 15:40:44 EST 2006 | mgdrouin1
Comp is relay. I've pulled the spec. Max 240. Using Leister h/g with manual temp settings from 1-6 (20 - 600C)set by the operator. Gun was set to setting 4. They are using the heat gun to reflow the solder after SMT but before wave. High fai
Electronics Forum | Mon Jun 08 14:19:30 EDT 1998 | Gary Simbulan
Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have
Electronics Forum | Sun Apr 25 12:05:50 EDT 1999 | Chrys Shea
| | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free solderin