Thanks to the emails and posts I've read I think I've narrowed the problem down. Its a Netscape issue (which is why when people first initially said they were having problems it was working for me.) I'm working to resolve the issue. In the mean ti
Electronics Forum | Sat Jun 03 03:35:16 EDT 2006 | mika
Yes we do have a problem with this. We have by now investigate numerous lead/RoHS PCBA:s The RoHS boards are by far the most difficult one's to probe and test. Our people at the "test area" including Flying Probe and ICT they spend a lot of time to t
Electronics Forum | Mon Jun 26 23:33:20 EDT 2006 | KEN
We saw this condition over 3 years ago. It sometimes is called "champagne bubbles". The intemetalic formation is interrupted due to the micro voiding reducing mechanical strength. I discovered this on lead free test vehicles for a major computer
Electronics Forum | Wed Sep 12 17:09:11 EDT 2007 | allwave
HI John, I use wave fixtures with titanium inserts. So far I have not seen any problem with walls about 0.010" thickness and 0.120" tall (or deep depending how you see it)...The Titanium-composite interface is also very strong (as long as you have e
Electronics Forum | Wed Feb 16 17:32:49 EST 2005 | russ
Public Beating? Yes,Yes indeed. So Duckmann how is this little problem coming along? Russ
Electronics Forum | Tue Mar 29 20:11:12 EST 2005 | KEN
If the granite is a problem, how about using some "stati-cide" type of spray.
Electronics Forum | Fri Aug 26 14:15:16 EDT 2005 | David
Where could I find more information regarding the double sided reflow and flux problems with white tin?
Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Wed Aug 21 19:22:44 EDT 2002 | stownsend
Splitting hairs is putting it mildly. I�m just trying to rule out all variables. It doesn�t appear that we have an SIR problem, but since the newest variable is OSP (blame the new guy for all the problems), I have to consider it. I�ve seen this befo
Electronics Forum | Tue May 09 14:49:57 EDT 2006 | Larry
Hey guys, Anybody having trouble with increased false contact issues in ICT after switching from lead to lead free? Our test guys keep trying to imply that the flux residues are a problem (we're using Alpha EF2202), but as the soldering process eng