Electronics Forum | Tue Oct 22 14:55:50 EDT 2002 | slthomas
Dave, are you telling me that yer tryin' to pawn that off as a superscript "degree" symbol??? Wass' wrong with 183C, fer criminy's sake? (fighting urge for more defensive ranting) I'd swear a couple of old posts changed the way they displayed after
Electronics Forum | Wed May 19 09:32:28 EDT 2004 | Mr Fix it - MPM
Sounds to me like the driver for the tactile is not working. The tactile has three components to it. The first is the switch, the second is the pneumatic up/down actuator and the third is a small motor in the tactile assembly. The motor has a driv
Electronics Forum | Tue Dec 18 08:08:09 EST 2007 | itwasbill
Hi all, How can I convince my equipment purchasing supervisors that to properly solder BGA's a 7 zone oven would be far superior than a four zone? We currently own a 4 zone oven and I'm fearful that the BGA will not get adequate heat for solder
Electronics Forum | Fri Aug 03 17:21:03 EDT 2012 | kmots15
We will be running a very large board with 62k+ components on it in the coming week. Has anyone run boards with this qty before? For sanity sake I had to split up the board into 12 individual programs. We will be forced to run it on a My12 due to
Electronics Forum | Fri Oct 22 21:35:54 EDT 1999 | se
It's IIT, not ITT. DEK in the UK also uses a tensioning frame, but I don't know of any suppliers in the US. As a stencil vendor without a quick mount/re-usable frame to sell, I can say that I have not heard many complaints regarding print quality o
Electronics Forum | Thu Dec 20 12:27:25 EST 2001 | seand
Hello Gentlemen, Dave has a good point. Proposing to move the rails for the sake of thermal integrity doesn't seem logical to address you issue. By adding a rail set you have simply added mass (almost like big heat sinks) throughout the oven vs. w
Electronics Forum | Wed Mar 24 20:19:09 EST 2004 | Ken
I recently did a no clean flux eval and by far the leader in the category for remainder (residue) was Interflux 2005MZ 1. You first mission is to provide acceptable solder joints. 2. Only apply what you need to achieve acceptable results. Spray f
Electronics Forum | Thu Mar 30 12:57:21 EST 2006 | cyber_wolf
Fuji has said a lot of things in the past, then changed it later on. Just for the sake of argument....The guys that have trained me worked at Fuji for a minimum of 12 years. Not quite sure what Tech is talking about, but I do not recommend doing w
Electronics Forum | Wed May 12 13:34:02 EDT 2010 | hegemon
Thanks Pete B - great info. I am currently preparing a DOE to address concerns about reflow of componentry on the bottomside of the PCB while in the vapor. Specifically cosmetics and part dropping. Bottom side has no flux, but will be fully reflow
Electronics Forum | Mon Aug 27 22:16:03 EDT 2012 | ilanhovan
Hi, my supplier is using the same Aqueous machine to clean the boards for 2 different customers. My product uses the chemistry of leaded clean flux meanwhile the other product uses the chemistry of lead free with no clean flux, however that product r