in all actuality, you are both right. Alpha metals does have the toughest/hardest noclean residue that I have seen. When changing to no-clean FLUX you should run different probes. So back to square one. You're both right so who's gonna win?
Electronics Forum | Mon Dec 18 13:00:47 EST 2006 | grantp
Hi, We have a white residue, which is visible, and we would like to have the produce clean as it's a PCI card, so users see the PCB. I am wondering if we need to install a cleaning stage to the line for these kinds of products. Can anyone give som
Electronics Forum | Wed May 20 17:00:56 EDT 2009 | dyoungquist
We just placed a 56 pin QFN, 1 per board, on 10 boards and had zero defects. A good paste job, proper placement and a correct oven profile are the keys. If these are set up correctly, on larger runs your defects won't be zero but they should be le
Electronics Forum | Thu Aug 27 08:27:00 EDT 2015 | fcmtechnician
Hi to everyone involve in this subject, Pls illuminate me on Line/Equipment/Product certifications! I understood that in factory with automotive products you need to certificate all equipment, materials, etc! I need to bring external company to do
Electronics Forum | Mon May 15 13:55:00 EDT 2000 | Aldo
We are in the process of researching manual or low cost automatic Tape and Reel equipment. I have heard about V-tek and Systemation. I would appreciate if someone can tell me any problems or virtues of theses two brands that have been experienced. Al
Electronics Forum | Wed Oct 10 13:35:00 EDT 2001 | stepheno
I used to work with Chris. (neither of us are there anymore). What is he talking about is putting components into "pockets". The parts would come in, in sticks (tubes) but we wanted them in reels. At first we sent them out to be reeled, but that w
Electronics Forum | Thu Jan 18 09:00:38 EST 2001 | bdoyle
Thanks to the emails and posts I've read I think I've narrowed the problem down. Its a Netscape issue (which is why when people first initially said they were having problems it was working for me.) I'm working to resolve the issue. In the mean ti
Electronics Forum | Thu Mar 31 23:14:18 EST 2005 | Steve
Russ if your asking me if covering the surface of the granite defeats the purpose then I'm lost. An ionizer is a very good suggestion but they are not inexpensive. If the table is grounded and the metal bars are on a grounded mat, laminate etc. then
Electronics Forum | Thu May 26 00:42:19 EDT 2005 | nicholas2005
Ok, I just need someone to give me some feed back on a few questions I have. If anyone could help me that would be great. Example: take a Fuji CP-4 feeder for instance! If I machine my own, place my own parts on it, and place my own company name, and
Electronics Forum | Wed Mar 12 23:00:10 EDT 2008 | davef
You can say: The pad was lifted after reflow and prior to the dye and pry failure analysis. When we see lifted pads, we think: * That's a good solder connection * Either it took a lot of force to lift that pad or the fabrication of the board in the