Electronics Forum | Thu Aug 05 12:59:16 EDT 1999 | John
I was wondering if anybody could tell what web sit rates the equipment in regards to speed? I was there before but forget the address. Thanks,
Electronics Forum | Mon Aug 09 19:39:47 EDT 1999 | ScottM
| I was wondering if anybody could tell what web sit rates the equipment in regards to speed? I was there before but forget the address. Thanks, | Check this website out, it has a few comparisons in the Equipment survey section. Cheers, Scott
Electronics Forum | Sun Aug 19 09:27:09 EDT 2001 | davef
Yano, imalookinat two vendor specification sheets that say your paste should sit around at "print temperature" for 1 to 6 hours before printing [er, words to that effect]. Werejallgit this 6 hours stuff from?
Electronics Forum | Wed Dec 05 11:35:15 EST 2001 | smtspecialist
What is the best way/material to clean leads with 20% copper exposed that have been sitting in a stock room for a couple of years. My process uses NC flux 263 from AIM and I want to stay with the NO-Clean as much as possible!
Electronics Forum | Mon Feb 18 08:30:28 EST 2002 | jax
Wolfgang, Billboarding is kinda like a tombstone. The part is just sitting on it's side instead of on it's end. There should be plenty of info on this in the archives under billboard and tombstone. Most likely cause is off center placement and ov
Electronics Forum | Tue Aug 20 14:18:06 EDT 2002 | larryk
Kevin, I saw a few months ago in a Philips pamphet that they now have a "tray" that sits at the feeder locations for loose components or a small tape of components. I think it was for the Topaz machine.
Electronics Forum | Sun Aug 25 07:15:55 EDT 2002 | cnoonan
What are the industry standards for eutectic solder-paste in conjunction with the life span of solder-paste. What is the recommended duration of solder-paste on a printed circuit board. Example: You print a board, how long can it sit before runnin
Electronics Forum | Fri Sep 20 16:00:11 EDT 2002 | dougt
If it keeps generating interest (other than sales promos) on a day to day basis then thats great. I would say that if it sits for 30 days it's probably now a resolved issue by its originator and its time to close it up.
Electronics Forum | Wed Dec 11 09:41:26 EST 2002 | davef
I'd guess that you need to sit at your current 216-218*C peak for that 5 to 10 seconds that I mentioned earlier. Increasing your peak is the easiest way to do that, as you say.
Electronics Forum | Tue Jan 13 07:44:48 EST 2004 | Chris Cottreau
Upon inspection were seeing most if not all of these SOT 23 are not reflowed properly. The components just sit on top of the solder, this is creating insufficients, poor wetting, etc. There are about 25 SOTS per board, 2 boards per panel creating alo