Electronics Forum | Mon Sep 06 19:59:59 EDT 1999 | armin
| | | We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these s
Electronics Forum | Tue Mar 25 08:29:33 EDT 2014 | sara_pcb
Please refer the attached jpegs, The problem is noticed after reflow soldering followed by conventional through hole soldering. Flux used one is MIL Std. Brush cleaning in IPA is followed after each soldering step. regards, R.Saravanan
Electronics Forum | Wed Feb 18 12:42:43 EST 2004 | babe
OK, if the sphere of the ball and the paste on the pad are both eutectic, 63/37 then the paste will reflow first causing a drop of the component, after which the spheres will reflow causing a double drop and a good intermettalic. You can see this by
Electronics Forum | Thu Apr 05 08:44:45 EDT 2007 | ck_the_flip
"Guest" is right, actually. CSP's are essentially BGA's, but typically the pitch and ball diameters are much smaller and in some cases, the pads of the CSP's can not be screen printed. If that's the case, you'd have to have flux-dip capabilities on
Electronics Forum | Thu Nov 30 16:14:33 EST 2006 | darby
Maybe ask your customer where they got this idea from? It is possible they may have even got this idea from some white paper or article where they are trying to explain something else and show drawings with no solder between the pad and lead. It may
Electronics Forum | Tue Jan 31 15:40:44 EST 2006 | mgdrouin1
Comp is relay. I've pulled the spec. Max 240. Using Leister h/g with manual temp settings from 1-6 (20 - 600C)set by the operator. Gun was set to setting 4. They are using the heat gun to reflow the solder after SMT but before wave. High fai
Electronics Forum | Mon Dec 22 11:09:21 EST 2008 | mfcat
We changed paste manufacturers rather recently and are now seeing SOT23s falling off after wave solder. These parts have a dual process... we stencil print paste, apply glue, populate then reflow. Only SOT23s fall off, chips are fine. We do not be
Electronics Forum | Wed Dec 24 11:23:22 EST 2008 | childs
I can't seem to locate any information/concerns about moisture entrapment in IC packages on the promary side in a double sided SMT assembly using water soluable solder paste when soldering the second side. A typical process would assemble/reflow/cle
Electronics Forum | Fri May 22 12:42:43 EDT 2015 | deanm
Sr. Tech, you are right in that there is no verification of the profile. We are a Class 3 high mix OEM. We have visual inspection after SMT. We have not seen problems with wetting, grainy solder, cold solder, charred boards, etc. that would indicate
Electronics Forum | Wed Nov 29 10:10:50 EST 2006 | M. Sanders
I'm sorry, Dave - I didn't make myself very clear. Yes, this space (not really a "gap") is filled with solid solder. For instance, if you place a gull-wing component in solder paste, after reflow, there will probably be a thin film of solidied solder