Electronics Forum | Mon Oct 02 12:43:30 EDT 2023 | daniel_stanphill
I agree with dontfeedphils. Any time we run into a moisture sensitive component that cannot go through our wash cycle, we solder the component(s) by hand after everything that can be washed has been reflowed and cleaned.
Electronics Forum | Sun Oct 19 19:01:20 EDT 2003 | harotec
Dave and Pete No bad words against a good batch oven. I don't know the APS-oven mentioned but check out the description of the unique temperature-feedback system in our Ecosold at http://www.reflowsystems.com/press/PressReleases.pdf . As a matter o
Electronics Forum | Thu May 26 08:52:42 EDT 2011 | davef
Phil Zarrow wrote a useful paper that could help in evaluating paste. Here read it ... Evaluating Solder Paste � Not An Option Contributed by Phil Zarrow of ITM an Independent SMT consulting firm With soldering being the dominant source of assembly
Electronics Forum | Fri Feb 13 12:16:05 EST 2004 | Mike Konrad
Ashok, It is most likely not the DI water that is attacking the aluminum rather it is the saponifier. DI water is only in contact with the parts for a relatively short time. If your cleaning process provides for a rapid drying cycle, you should be
Electronics Forum | Tue Sep 05 16:04:43 EDT 2000 | Dave F
Pascal: Responding to your questions: 1 Do we have to dry the PCB after cleaning (sic)? Generally, nothing says you have dry the PCB after aqueous cleaning. Along this line, I received several thoughtful responses when I posted a similar thread.
Electronics Forum | Thu May 06 01:37:56 EDT 1999 | Kallol Chakraborty
| I would like to know if someone aleady have problems with Ceramic Capacitors SMD in In-Circuit Test (see below)and how did you solve this problems ? | | PROBLEMS | 1 - Only one kind of capacitor (2n2F), of all capacitors on board, sometimes are o
Electronics Forum | Mon Oct 12 08:07:45 EDT 1998 | Earl Moon
| I have datas to substain that a not wetting PCB ( the HAL oxided or not uniform in thickness )if soldered in reflow, it shows voids with X-Ray inspection.The voids are in side all the joints not only on the solder pads levell. | | Is there a techn
Electronics Forum | Fri May 07 02:29:16 EDT 1999 | Bob Willis
| | I would like to know if someone aleady have problems with Ceramic Capacitors SMD in In-Circuit Test (see below)and how did you solve this problems ? | | | | PROBLEMS | | 1 - Only one kind of capacitor (2n2F), of all capacitors on board, sometim
Electronics Forum | Mon Aug 10 21:52:34 EDT 1998 | Dave F
| | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not
Electronics Forum | Tue Aug 11 07:51:57 EDT 1998 | Earl Moon
| | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, n