Electronics Forum | Tue Jun 29 14:42:55 EDT 2004 | davef
You're correct, for every dumpster full of paper written about solder, there's a sentance written about fluxes. There's dribs and drabs about fluxes in most of the soldering books [ie, Manko, Klein-Wassink, Judd, Strauss, etc] and most of that is ve
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Jun 28 00:11:30 EDT 2016 | ricoloverde
Hi, new to the forum here. First Post! Ive been using a Samsung sm482 for about 2 years and recently got the heads up that we will be getting a project soon with a BGA chip. Im wondering if anyone on here uses the SM482 for BGA and if so, can offer
Electronics Forum | Tue Aug 22 03:04:07 EDT 2006 | PP
Any help/suggestion is much appreciated I am doing lots of BGA Reworks from a small uBGA with a few balls to a large BGA with over 1500 balls. The reworks have been done on SRT 1100 Series Machine for many years. SRT 1100 Machine is good for the c
Electronics Forum | Mon Jan 10 18:35:05 EST 2011 | eadthem
Ive used a Mirtec machine for 3 years MV3L with side angle inspection. Mirtec has some issues documentation, and repair plus. But there machine is impressive and the AOI software is good. We can find about 90-99.99% of all errors using just the 5
Electronics Forum | Mon Jan 15 13:12:18 EST 2007 | realchunks
So others can solder the same board and part but you can't. Dipping the legs in flux doesn't help. Then it's either your pre-heat or wave. Measure your pre-heat and compare to others or flux mfger. Do you have chip wave or something like an Omega
Electronics Forum | Mon Dec 22 11:09:21 EST 2008 | mfcat
We changed paste manufacturers rather recently and are now seeing SOT23s falling off after wave solder. These parts have a dual process... we stencil print paste, apply glue, populate then reflow. Only SOT23s fall off, chips are fine. We do not be
Electronics Forum | Tue Mar 25 13:55:05 EDT 2014 | horchak
Ok lets put it this way. If the PCB house used a high quality mask and properly applied it to a properly cleaned surface and properly cured it, then as Dave stated above there are only two things that can destroy it. Excessive heat and overly aggress
Electronics Forum | Fri May 23 18:55:20 EDT 2008 | gregoryyork
This is one of the biggest mistakes with the Lead Free process. We have all listened to the 'industry experts' and followed their advice and unfortunately got it wrong. Keep the dwell times (dependant on alloy selection) the same as Leaded so you are