Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Tue Aug 26 17:02:10 EDT 2008 | allwave
What brand of flux and wave solder machine are you using? George
Electronics Forum | Tue Aug 26 13:44:14 EDT 2008 | cgray
The chain and fingers for our Wave solder is getting a large amount of residue from the flux (high dissolved solids) we are using. Any recommendations for products that can clean polymerized flux.
Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram
Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle
Electronics Forum | Tue Aug 09 13:51:03 EDT 2005 | patrickbruneel
You can also insert a stainless steel screw the size of the hole in the board before wave soldering, this will prevent the solder from wicking up to the top or close the hole (this is real cheap). I still remember the good old days using toothpicks t
Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS
It may be you should look for higher TG of Durapol Rgds GS
Electronics Forum | Wed Aug 27 08:00:33 EDT 2008 | cgray
We are using Multicore (MFR 301) from Henkel.
Electronics Forum | Wed Aug 27 14:07:42 EDT 2008 | cgray
Thanks for your experiences.
Electronics Forum | Mon Dec 16 16:35:55 EST 2002 | Jim Ferris
Randy, Steve & all, Can you guys point me in the right direction when it come to using selective wave soldering...I am trying to get in-depth information on the Pro's & Con's of having our supplier use this process for our PWA's. (I can see there ar
Electronics Forum | Wed Jan 26 20:52:06 EST 2005 | Chua
Hi, I'm going to evalute new solder paste and flux for wave-solder. Appreciate you could advise what are the things need to look out during the evalution. Any recommend step or proper way of doing solder paste and flux evalution. Appreciate your he