Electronics Forum | Wed Nov 06 12:56:10 EST 2002 | slthomas
What I'm seeing is an occasional pattern of tear drop shaped features in a sea of nice shiny solder. The little islands don't really have any relief.....it's more of a surface finish feature than a 3-dimensional feature. The wetting angles are good,
Electronics Forum | Wed Oct 24 13:23:29 EDT 2007 | hussman
Good points on both subjects. Not all who talk engineer speak are engineers. It depends on how shiny their shoes are. Delta T across any medium can mean a myriad of different set values. From Polynomial Expressions to the names of any organization
Electronics Forum | Mon Sep 23 12:58:13 EDT 2002 | dragonslayr
Methusala was very old yet he is still talked about thousands of years later. In my perspective, age of a thread is not the issue. It is the careless resurrection of a non-active subject that causes waste of time and space that is the issue. I can
Electronics Forum | Tue Jan 20 07:57:00 EST 2009 | mrdtech
Depends on the solder paste. If it has been on the stencil for 24h there is a good chance that the paste is destroyed. You can however check if it has not dried out too much by letting the stencil printer do a few strokes and see if the paste still h
Electronics Forum | Sun Jan 18 09:20:26 EST 2009 | davef
We're not sure of the condition of your solder paste. So, afte 24 hours, if it's: * Unused, in a reclosed container, maybe a week of life depending on the environment * Used, scrap A simple coalescence test can quickly determine the condition of sol
Electronics Forum | Fri Jun 02 14:42:06 EDT 2023 | tommy_magyar
"If for example a customer requested assemblies but never specified their requirements, would MFGs be expected/required to follow parameters from a specific class related to the end use of said product?" Answer: The customer placed an order with you
Electronics Forum | Fri Aug 02 11:06:39 EDT 2019 | robl
Personally I'd take a Metcal MX500 over a 130W JBC every day, and we had hundreds at the last place. However, here we have lots of JBC's, and my engineers and solderers swear by them. Both are good irons and like any you need to get your tip choice
Electronics Forum | Mon Jan 21 11:12:20 EST 2008 | davef
Just what is delaminationg during testing? Water washing should be sufficient to clean WS609. On the other hand, it's possible you're conveyor speed is too high to do a good job cleaning the high density areas. What kind of testing have you done to
Electronics Forum | Thu Aug 31 08:43:40 EDT 2017 | hxamalia
Hello dear Good day , it is Amalia from HX Circuit Technology Co.,Ltd in China, we are a prefessional PCB factory with many years. We forcus on producing Aluminum PCBs for LED , please contact with me now ,thanks Email: amalia@hx-circuit.com Skyp
Electronics Forum | Wed Oct 11 16:24:35 EDT 2000 | John Thorup
Hello Antonio ASPECT RATIO = the ratio of one dimension to another as in the ratio of the thickness of a stencil to the width of the aperture. For instance, a 10 mil aperture in a 5 mil stencil will have an aspect ratio of 2. This is aperture width