Electronics Forum | Thu Feb 10 22:41:20 EST 2000 | Dave F
Russ: Now that�s a good story. Nuff said on the Vegas trip, that explains everything. Especially when you say "it must have something to do with ..." I love WS609. It�s been berry, berry good to me. Intermetalic Layer (IL). A compound formed a
Electronics Forum | Thu Feb 10 04:07:29 EST 2000 | Wolfgang Busko
Jeff: We had a similar problem a couple of years ago with boards from one specific subcon. At first sight the joints looked well formed sometimes with a little bit more sometimes with a little bit less solder but still in limits not to be worried abo
Electronics Forum | Tue Dec 26 12:35:09 EST 2000 | Dave F
Your English is fine. Your assessment that corrosion on a portion of the metalization on the end of a component is causing the tombstoning is reasonable. We've seen that before. Corroded components received from a supplier is not acceptable as an
Electronics Forum | Tue Oct 03 20:35:23 EDT 2000 | Dave F
1. Throughput * Dispenser: Slower, may loose 70% of tact on fast chip shooters * Printer: Can be put in front of and use fast chip shooters effectively 2. Rework Rate ???? Deposition control???? * Dispenser - High control over amount paste - Coplan
Electronics Forum | Wed Sep 06 11:18:52 EDT 2000 | Chris May
Randy, I have been with my present company about 14 months and my first and ongoing task is to improve 1st time yield rates at ATE. Upon examination of the failures (14 months ago)there were cases of IC legs being physically wider than the pads on
Electronics Forum | Sun Aug 06 14:02:04 EDT 2000 | David Harper
The company I work has been assembling this particular board for several years now, and one thing has always remained constant. Bad Soldering. The board is a double sided board, the solder side has about 250 1206 caps & resistors and Sot-23 transisto
Electronics Forum | Fri Jun 16 06:24:43 EDT 2000 | Wolfgang Busko
Hi Todd, it might be a philosophical question if soldermask between finepitch pads is prefered or not. That should depend on the capabilities of a particular site and their experience. We actually prefer soldermask down to 0,4mm pitch and don�t have
Electronics Forum | Mon Apr 17 18:42:32 EDT 2000 | Russ
Murad, I have just completed a switch over in our facility to no-clean. We used Alpha 609 and 857 paste and wave flux respectively. We currently use Alpha UP78 paste, NR330 wave flux, NR205 liquid flux for touchup and cleanline 7000 wire solder as
Electronics Forum | Wed Mar 14 11:51:24 EST 2001 | fmonette
Popcorning is the common designation for defects related to the moiture sensitivity of plastic molded components, like PBGAs. The plastic body of these parts will absorb moisture from the ambiant atmosphere on your factory floor. If a critical level
Electronics Forum | Wed Mar 14 18:17:40 EST 2001 | mparker
Some thing to watch out for is the cure spec for the adhesive. Will that match with your solder paste reflow spec? You will have two dissimiliar materials going through endothermic reactions at the same time. You could end up with under cured adhesiv