Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Tue Nov 06 22:37:35 EST 2012 | davef
Ryan ... "As for bismuth-based lead-free alloys, a lower melting temperature than that of tin-lead is offered together with a cost similar to that of tin [in the area of $3/lb]. Unfortunately, bismuth in soldering alloys tends to create embrittlemen
Electronics Forum | Wed Nov 07 15:01:18 EST 2012 | nikyta
Thanks Dave , my question is about Spopov want to try "Lead Free" SnBi (but uses it on Leaded finishes), but is worry about its low melting point (at this point, no longer 138 degrees as he wrote, but rather in an unknown and unpredictable range bet
Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Thu Mar 23 21:35:43 EST 2006 | Wave Master Larry
Eutectic is were the deltas of the oven melt the paste. At least that what the maintenence guy tells me but hes alway gooped up on some goop, so who really nows. No lead is simple. With all the cell phones you guys by nowadays, the gabage heaps ar
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Mon Feb 18 13:11:41 EST 2008 | tonyamenson
Are there profilers that I can use over my leaded and lead-free wave that can also profile my reflow ovens (leaded and lead-free). I'm not that familiar with either but as I learn I can't help but think that there should be something on the market t
Electronics Forum | Tue Mar 11 16:18:45 EDT 2008 | markhoch
We purchase our Biral T&D, Visco Grease, and NMT (No Melt) Grease from: Biral USA P.O. Box 878 McLean TX, 79057 ph (806)779-2700 fax (806)779-2543 Hope this helps!
Electronics Forum | Wed Jun 05 17:13:58 EDT 2002 | Yannick
Hello! I have a strage problem, we made some production with uBGA, BGA, 0201, 0805, and other type of component. We didn't put the uBGA and 0201 and BGA on the board at the end of the line we look a our solder joint and surprise the solder made a