Electronics Forum | Thu Aug 24 08:47:32 EDT 2006 | russ
We reduce 50% on that pad and achieve excellent results as well. Have placed somewhere in the hundreds of thousands of these (one board we have has 75 alone!!!) We do nothing special for other pads. Russ
Electronics Forum | Wed Mar 21 05:19:25 EDT 2007 | Rob
Please can you stop murdering our beautiful language! It's pronounced soul der. You see, this is what happens when you leave the colonials alone to look after themselves for a few hundred years! ;)
Electronics Forum | Wed Oct 10 07:54:50 EDT 2007 | shrek
Hussman,I'm quite happy to exist alone in his swamp and dine on delicacies like pickled eyeballs. This means you, me lad. BACK OFF!
Electronics Forum | Thu Dec 13 13:56:24 EST 2007 | greg_diaz
I would like to know if anyone out there is using a stand alone Board labeling equipment and what type.
Electronics Forum | Tue May 27 13:24:44 EDT 2008 | tech1
We traded in old vibes for this thing and wished it was around long ago. The savings in lost parts and set up time makes it worth it alone.
Electronics Forum | Thu Nov 20 07:23:22 EST 2008 | hussman
The process materials alone will cost you more than a half dozen stencils. Not to mention the labor involved. Then the cost of all the equipment involved? Jeez, how do people like this make it to power?
Electronics Forum | Mon Mar 01 09:36:29 EST 2010 | duanebrayton
Good morning Chris, We had discussed surface tension but were not sure if that alone would be enough, so I reduced the bottom side temperature in the oven by 20 degrees to see if that would help. I will be checking results this morning. Thanks f
Electronics Forum | Tue Jun 08 14:01:30 EDT 2010 | smtmax
Hi Danny, What is your application? Maybe I can assist you. We carry several different type of reflow oven. I have from tabletop to conveyor stand alone reflow machine. Let me know. Best Regards, Vee
Electronics Forum | Mon Aug 16 17:02:51 EDT 2010 | martingruber
Hello I think I have to define the machine in Stand-alone modus, but I don't know how. I cn't find how in the manual. Thanks. Best regards M Gruber
Electronics Forum | Thu Apr 28 22:10:02 EDT 2011 | Jacki
Dear Dave Thanks for your advice.I dun know why flux can't use alone w/o adding other solvents. is it neccessary? Now, our flux density is 0.88. By the way, we use Hi Grade Flux 1080.