Electronics Forum | Fri Aug 27 11:27:55 EDT 1999 | Brian
I have looked through the IPC web page and surfed to frustration. Can somebody give me a lead?
Electronics Forum | Sat Aug 28 09:23:36 EDT 1999 | Mike McMonagle
| I have looked through the IPC web page and surfed to frustration. Can somebody give me a lead? | Check out the EasyBraid website below, they carry IPC standard coupons, flux test kits and SIR meters at reasonable prices.
Electronics Forum | Mon Aug 30 16:10:10 EDT 1999 | Dave F
| I have looked through the IPC web page and surfed to frustration. Can somebody give me a lead? | Brian: We don't use an etched board. We use a special stencil, described below and print on bare copper laminate. 3 Solder Wetting Test. Recogniz
Electronics Forum | Thu Aug 24 15:54:13 EDT 2006 | davef
It depends. What is: * Storage environment and period * Board laminate, epoxy, and copper thickness of PTH * Down stream process * Etc FR4 0.062" thick boards absorb between 0.08 to 0.1%Wt of moisture within a 24 hour period, and 0.2 to 0.23%Wt in
Electronics Forum | Fri Oct 16 14:36:11 EDT 1998 | Jeff Sanchez
| With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to overco
Electronics Forum | Fri Oct 16 21:17:04 EDT 1998 | Scott McKee
| | With current soldering of stranded wires to pcb assy's the wire tends to be very brittle and can break with very little movement of the wire. We use a low residue cored wire. Anybody with advice or who has seen a similar problem/knows how to over
Electronics Forum | Thu Oct 11 22:25:50 EDT 2001 | davef
Bruce I�m with yall. Designers and fabricators say �pins�. You say: * BGA pins are 1mm [0.039�] pitch. * BGA pads are 0.4mm [0.0157�] diameter. * BGA pins are 0.6 mm [0.024�] side-to-side. * Board thickness is ~0.4 mm [0.015�] First, as you can
Electronics Forum | Mon Sep 06 20:18:37 EDT 2004 | charly
hi, we are running high mixed low volume here, and i encounter many pcb delam after reflow issue. here some doubt need ur advise: 1. actually, what is max temperature and duration can a bare PCB reflow without any quality problem? if i allow bare
Electronics Forum | Wed Apr 06 15:41:53 EDT 2005 | Dirty Boards
Any help locating a machine to remove foreign materials from bare pcb's would be appreciated,
Electronics Forum | Fri Jul 31 12:53:58 EDT 2009 | dyoungquist
On our Mydata machine, we place a piece of scrap bare pcb next to the pcb we are loading. Using double sided tape, we attach the cut tape strip to the bare pcb, then program the machine to pick up the parts from that location. The smallest Mydata m
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830