Electronics Forum | Thu Feb 10 16:00:31 EST 2000 | Travis Slaughter
I have had cases when it was necessary to run epoxy and paste at the same time. The only good reason I know of to even think about messing with going to this trouble is if the surface tension of the solder melting pulls the part out of alignment. T
Electronics Forum | Thu Jul 06 03:03:56 EDT 2006 | ronalds
Thank you all for your input. The MF300S Multicore flux is rated for lead free. There is not much dross or contamination. We are using nitrogen. I've tested the boards with the curing test of IPC-TM-650. I think you're all right about the preheat.
Electronics Forum | Tue Jan 23 10:15:44 EST 2007 | slthomas
J-STD-001C just requires that the area not be so dirty as to contaminate your product, tools, workspace, etc. If you start counting particles, you're into cleanroom territory. Do a search on ISO 14644-1 for specifics. Actually Wikipedia does a ni
Electronics Forum | Tue Apr 11 10:30:46 EDT 2000 | Jeremy Smith
I am having a problem with some joints on a 100 pin pqfp and few different soics on one particular board. When viewed a 8x with a "Mantis" inspection scope the joints look as though they wetted to the ic leg but when probed the leg will pop loose.
Electronics Forum | Thu Apr 21 11:43:03 EDT 2005 | davef
We understand the problem of trying to coat over RTV. We have seen the same problem with acrylic and urethane coatings not wanting to stick to RTV. Some acrylics seem to be worse than urethane. Since this is a new product, may be you could pot your
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Fri Dec 17 14:20:01 EST 2004 | Claude_Couture
CO2 is not the problem, CO (carbon monoxide) produced by combustion (engines,fires, etc) is. Trees and vegetation can process CO2, but not CO.
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc
5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl