Electronics Forum | Tue Jul 27 13:48:45 EDT 2004 | Ralf
Hi Recently i have noticed that after reflow (hot air oven) on the solder lands without components but with solder(screen printing) there is discoloration. It looks like gasolin spilled on the wet road (rainbow). Any idea and reason Ralf
Electronics Forum | Tue Jan 15 06:05:37 EST 2002 | Romain
Dear all We have since few weeks problems with BGA solder joint integrity on ENIG finish. Under relatively very flexible of the FR4, the joint breaks between ball and PWB. When we take off the BGA for analysis, some of the pads seem very flat, totaly
Electronics Forum | Tue Feb 08 04:27:55 EST 2011 | thomas111
hi, I am a Hardware designer . One of my products is undergoing a Reliability test in which a resistor shows a high value on board from its specified value .However it retains the original value when its cooled under room temperature. The resistor
Electronics Forum | Tue Jan 15 12:20:16 EST 2002 | cfraser
This sounds like it could possibly be a case of Black Pad. We have had a few issuses with this in the past as well. Who the PWB vendor? I also recommend searching the archives and doing some solder samples with nonpopulated boards
Electronics Forum | Tue Jan 15 09:42:40 EST 2002 | davef
Here's two choices. 1 Before accepting a lot of boards from your supplier: * Print some paste on a board * Reflow the paste * Inspect the quality of the solder connection * Make a decision on accpting the board based on that observation. 2 Have yo
Electronics Forum | Mon Jun 12 06:45:10 EDT 2000 | kim ji tae
Hi! Thanks all who upgrade these pages. I have some questions. Is there any answer? I do double-sided reflow solderig, with 0.4% AG solder cream. with AU finished pcb. First I do reflow solder bottom side where 0.5pitch TQFP locates. Second I do re
Electronics Forum | Fri Feb 01 11:58:28 EST 2002 | Romain
the PCB vendor is Multek in germany he made some measures about P content in Ni layer. What is the normal level of Phosporous and what is the upper limit ? thanks Romain
Electronics Forum | Wed Jul 28 17:34:27 EDT 2004 | Steve Stach
Hi Ralf, This discoloration may be re-oxidation. Fluxes are supposed to do three things (1) remove oxide, (2) promote wetting, and (3) protect surface from reoxidation. The solder paste possibly is not protecting from reoxidation. Best Regards, St
Electronics Forum | Wed Jan 16 20:06:09 EST 2002 | davef
No, not as such. Consider: * Using the IPC calculator [free at http://www.ipc.org]. It allows you to consider / assess the amount of solder when designing pads. * Reviewing IPC-7525 - Stencil Design Guidelines. It gives general aperture guidelines.
Electronics Forum | Mon Jun 12 22:00:51 EDT 2000 | Dave F
Could be. What are your profiles? 2) Au finish fail => Could be, but that the connections can be made with hand soldering makes this a low probability cause, assuming the activity of the flux used in hand soldering is not significantly different fr