Electronics Forum | Mon Feb 02 06:55:13 EST 2004 | Sam
The Type we predominntely use is Acrylic, but we also get this problem when we use silicone or urethane. Sam.
Electronics Forum | Tue Feb 10 13:59:29 EST 2004 | Vadim
At times the orange peel effect can be from excess flux improperly removed. Our company strictly provides the service of selctive conformal coating application. We quite often see this. Most times if the board is simply "water washed", or IPA washed,
Electronics Forum | Tue Feb 10 14:02:03 EST 2004 | Maryann
At times the orange peel effect can be from excess flux improperly removed. Our company strictly provides the service of selctive conformal coating application. We quite often see this. Most times if the board is simply "water washed", or IPA washed,
Electronics Forum | Mon Jan 26 19:51:48 EST 2004 | davef
You should be able to obtain a smooth finish. A "glass-like finish" is in part a function of the coating material, assuming good process. When we see "orange peel" conformal coating, we think moisture from the spray room environment, conpressor, et
Electronics Forum | Fri Dec 10 12:24:46 EST 2010 | davef
Causes of dewetting in conformal coating. Factors that influence dewetting usually involve non-ionic contamination such as: * Residues from board manufacture including silicone surfactants from solder resist & HASL rinse contamination * Component res
Electronics Forum | Wed Jul 07 17:23:13 EDT 2004 | davef
Contact: Graham Naisbitt; Concoat Ltd; graham.naisbitt@concoat.co.uk [We have no relationship, nor receive benefit from the company referenced above.]
Electronics Forum | Mon Apr 04 13:06:01 EDT 2005 | davef
Here you go: * Wood sealing http://www.paintdocs.com/webmsds/webPDF.jsp?SITEID=DURA∏no=86300000&doctype=MSDS〈=E * Board sealing http://www.mgchemicals.com/msds/english/liquid/4223.pdf
Electronics Forum | Thu Jul 07 00:53:12 EDT 2005 | Gary Bremer
Curtiss-Wright uses MIL-I-46058 at present. Any suggestions on how to approach engineering and update the drawings for new contracts?
Electronics Forum | Fri Apr 17 08:52:03 EDT 2015 | charliedci
Thanks for the info Sarason. The UVCL is a Urethane. Did not want that hard of finish (for solder rework issues). We like the Acrylic as acetone will remove cured material for solder rework.
Electronics Forum | Tue Mar 06 17:14:40 EST 2001 | bschwyn
Is conformal coating necessary for products that are used indoors?