Electronics Forum | Tue May 24 21:48:23 EDT 2005 | steve
You can continue repair and rework with tin/lead solder until 7/06. However!!! Any product still on the shelves overseas after 7/06 will be returned to the USA. Thought? Maybe start repairing with SAC305 now? Also SAC is Tin, Silver and Copper. No Ni
Electronics Forum | Tue Apr 01 09:58:52 EST 2003 | davef
You're entirely correct. The gold is most likely gone away. [Don't forget you can check if the surface is still solderable with a hand soldering iron.] We're not sure it it will give you the results you seek, but consider using a dye penetrant fai
Electronics Forum | Mon Jan 04 18:56:25 EST 1999 | Marc P.
| We have a Vitronics SMR400N oven and many times need to use N2 inerting. My problem is that it takes close to an hour of operation to purge the system to achieve the desired O2 levels (~40PPM). This is not only time consuming but results in an inor
Electronics Forum | Mon Jun 28 13:12:34 EDT 1999 | Graham Naisbitt
| | We are anticipating switching from RMA to OA flux for both reflow and wavesolder in the next few months. If you use a batch cleaner running DI water only I would like to hear your experiences. How is it for cleaning under low standoff component
Electronics Forum | Fri Oct 18 17:04:38 EDT 2002 | ereno
We have a connector mfg that claims that their design is good and does not contribute to the problem that we are having. The problem is evidence of poor soldering. All other components that surround this connector have very good solder joints, with t
Electronics Forum | Thu Jan 29 15:30:41 EST 2004 | pjc
Rick, As I understand your comments, you do not need to clean off the flux residues? Then hot water and a little cleaning chemistry should do. However, there may be some reaction by the residual flux if not enough cleaning chemistry is used. There a
Electronics Forum | Thu Sep 16 18:09:28 EDT 1999 | Earl Moon
| | | Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | | | | | | | Although I agree that Earl would do a fine job setting up your facility, I do believe that it would be m
Electronics Forum | Thu Sep 16 18:51:52 EDT 1999 | Scott Cook
| | | | Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | | | | | | | | | | Although I agree that Earl would do a fine job setting up your facility, I do believe that it wo
Electronics Forum | Thu Sep 16 18:58:21 EDT 1999 | Earl Moon
| | | | | Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | | | | | | | | | | | | | Although I agree that Earl would do a fine job setting up your facility, I do believe th
Electronics Forum | Tue Jun 22 13:29:29 EDT 1999 | Deon Nungaray
| We're a CM doing low volume/high mix and are considering buying from one of the two big names, TR** or Sp*******/El*********. We need saponified wash for some of our no-clean over wave; the great majority is OA from our SMT lines. Any thoughts? |