Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Electronics Forum | Fri Oct 01 01:25:55 EDT 2021 | sn
Thank you Djo for your sharing. By the way, do you know that which field/product will prefer to use SAC405 paste instead of SAC305 or lower Ag wt% alloy solder paste?
Electronics Forum | Mon Nov 14 10:10:52 EST 2005 | davef
When soldering your full tin (no lead) and Pb95/Sn5 solder components, you need to modify your PbSn reflow recipe to compensate for the higher melting point of the changed solder alloy [with your Sn62/Pb36/Ag2 solder paste] on those component leads.
Electronics Forum | Thu Sep 23 08:08:12 EDT 2021 | SN
Hi. Anyone in this forum experienced the lead-free solder paste SAC305 and SAC405? What are the differences to expect for solder paste with SAC305 and SAC405? What is the effect of silver (Ag) alloy in solder paste? It was really appreciated if could
Electronics Forum | Thu Nov 10 08:23:35 EST 2005 | arclightzero
Hello, I am currently trying to isolate internal fallout problems with very low yield substrates mixed with great yields and have recently found that we are using a Sn62/Pb36/Ag2 solder paste with full tin (no lead) components as well as Pb95/Sn5 sol
Electronics Forum | Thu Sep 23 08:47:25 EDT 2021 | majdi4
1)Though in many cases the difference between SAC305 and SAC405 was small,and not always statistically significant, it was observed that SAC405 generally outperformed SAC305 joints. Under 0°C to 100°C thermal cycling,no statistically significant
Electronics Forum | Mon Dec 11 20:44:37 EST 2006 | davef
Title : LEAD-FREE WAVE SOLDER FLUX EVALUATION Author : Michael Havener Author Company : Benchmark Electronics, Inc Date : 09/25/2005 Conference : SMTA International Abstract : The European Union�s deadline to ban lead in electronic pr
Electronics Forum | Thu Jun 26 04:34:49 EDT 2003 | emeto
Hi James, I saw very good posts here.Now I will give you one more practical way: 1. My advice is to encrease the temperature(like your first sidgestion). Termostress is important thing so your first zone should be 120-150C. 2. The paste profile. If
Electronics Forum | Tue Aug 24 14:49:58 EDT 2004 | jamyboy
Hi, I am trying to assemble a LTCC component > with Pd/Ag surface finish on to Sn/Pb/Ag solder > and Sn/Ag/Cu solder. I am passing it through a > reflow. I have observed poor wettability at the > solder-pad joint. Does anyone have information