Electronics Forum | Thu Nov 21 11:10:07 EST 2013 | luciano
Hello, We've just started using VIGON A200 in our Aqueous Trident XLD system and observed that aluminium electrolytic capacitors get corroded. Concentration was set at 20% and washing is done by spray at 150F for 6 to 8 minutes. Then is rinsed seve
Electronics Forum | Fri Sep 07 14:55:25 EDT 2007 | jseagle
Change to through hole or hand solder. we are in the same boat and have not foound a reflow solution. James
Electronics Forum | Mon Sep 10 11:16:37 EDT 2007 | russ
Can you implement a longer soak? how many feet of heat do you have in oven? Russ
Electronics Forum | Thu Jun 19 12:48:32 EDT 2008 | mumtaz
What the hell our you talking about 200 c max? I would think any nolead part is capable of going hi-er that this. I think you are looking at max temps or something that does not make sents for temps you need to reflow.
Electronics Forum | Thu Jun 19 14:33:57 EDT 2008 | realchunks
My board reaches 240 C for 45 seconds. Most of my lead free parts require 230 C for a minimum of 30 seconds.
Electronics Forum | Thu Jun 19 15:07:23 EDT 2008 | realchunks
Sure! But they warm up slower than everything else, so it's not a big deal. You can taylor your profile around them and never exceed your 50 second threshold.
Electronics Forum | Sat Nov 15 08:07:09 EST 2008 | davef
A tenative yes. The hesitance comes because it seems that you're setting us up for something. So, howbout you tell us just what's going on?
Electronics Forum | Wed Nov 19 02:30:30 EST 2008 | lococost
... or try the IPC technet http://listserv.ipc.org/scripts/wa.exe?A0=TechNet
Electronics Forum | Tue Dec 02 02:47:54 EST 2008 | act_smt
Thanks for the resources. I plan on contacting them to get some answers. I hope this all works out for us & can help others someday should they come accross similar issues too. Thanks again.
Electronics Forum | Thu Nov 21 12:06:16 EST 2013 | rgduval
The last time I got corroded parts out of my wash was when my DI tanks were spent, and I was pretty much using straight tap water. Refreshing the DI tanks eliminated my issue. Hope this helps. cheers, ..rob