Electronics Forum | Thu May 22 12:32:35 EDT 2008 | tonyamenson
So here is my problem with the info you gave. If my preheat topside max is 150 - 170 C but my flux calls out a topside temp of 93 - 104 C..... ....Im pretty much up a creek becuase of a poor flux choice? FYI. we are using the Indium 3590-TX for bo
Electronics Forum | Mon Jan 15 09:19:29 EST 2007 | tk380514
We use Alpha EF-2202 low-VOC No-Clean flux Selective wave soldering cassettes Bottom pre-heating wave soldering machine We have one component that will not solder properly: http://www.epcos.com/web/generator/Web/Sections/ProductCatalog/Capacitors/Ul
Electronics Forum | Tue Feb 08 16:09:09 EST 2000 | dean
Generally speaking with most electronic grade epoxies: 1. Cure time is a function of temperature. 2. Polymer bonds begin to quickly break down above certain temperatures (product specific). I believe aprox 170-180C. The strength of the bond de
Electronics Forum | Wed May 21 13:59:19 EDT 2008 | pjc
Here's what I've seen for no-clean flux applications: Leaded: Dwell Time is? 2 - 3 seconds Top side board temp max? If some small SMT parts reflow are we too hot? 110 to 120C top side board temp just before hitting the wave(s) Pot temp. 245C Lea
Electronics Forum | Thu Dec 10 22:36:03 EST 2020 | solderingpro
I represent PROMATION USA and we have several solutions for solder wire perforation: Our QUICK 372B is a stand-alone drilling station. Our QUICK 371DI is a semi-automatic hand soldering station with perforation technology. Our QUICK 300A/B is a d
Electronics Forum | Mon Apr 12 19:28:26 EDT 1999 | Tom B
Netters, When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? 1. Kester 293 no clean 2. 2.1 C/s for 30s to 150 C 3. .5 - .7 C/s for 60s to 185 C 4. 1.5 C/s u
Electronics Forum | Fri May 23 18:55:20 EDT 2008 | gregoryyork
This is one of the biggest mistakes with the Lead Free process. We have all listened to the 'industry experts' and followed their advice and unfortunately got it wrong. Keep the dwell times (dependant on alloy selection) the same as Leaded so you are
Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc
5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht
Electronics Forum | Wed Dec 04 14:09:52 EST 2002 | Vince Whipple
By the way, what type of preheaters do you have? IR? Convection? If you have IR, there may be a way to cheat. Vince W
Electronics Forum | Thu Dec 05 11:04:27 EST 2002 | slthomas
They're IR, bottom side only. Frankly wave solder is not my forte (there are those that would claim nothing is), but I've personally been tasked with developing a process to do reliable, high volume bottom side SMT, so I'm drawing a lot from the tec