Electronics Forum | Wed Sep 30 11:32:45 EDT 2009 | pbarton
What type of conformal coating are you using and are you allowing the coating to migrate under the device in question? If you are allowing the coating unbder the BGA the problem could be CTE of coating is much greater than that of the BGA balls/sold
Electronics Forum | Thu Oct 08 08:15:39 EDT 2009 | kpm135
We've used both 1A33 urethane and 1B31 acrylic coating on our SMT assemblies with great success for many many years. This is with components of all shapes and sizes including a 9 ball micro-BGA. We apply the coating in every way imaginable and we hav
Electronics Forum | Mon Sep 16 13:29:37 EDT 2013 | larrygroves
a lot depends on the age and type of equipment you are using . Older equipment can have a lot of problems with smaller parts. If all is well with your feeders and machine you should expect something like 99.8 to 99.9 percent. some parts will be ident
Electronics Forum | Wed Sep 18 15:41:59 EDT 2013 | cbeneat
For 0402's, if the operator is paying attention, our equipment Panasonic CM 402/602/NPM's run at about .001%. Again this is dependent on an operator that pays attention to the fail rate. We usually don't have too many problems with 0402's, LED's ar
Electronics Forum | Wed Dec 14 12:34:56 EST 2016 | cy4223111
Hi all, Recently, we are trying to do wire bonding between a 75 * 75 um pad on a chip and substrate with 150 um height difference, but when completing wire bonding and the wire bonds on pad and substrate, the pad will get out of the chip easily
Electronics Forum | Wed Dec 14 20:17:48 EST 2016 | davef
As I understand, you are wire bond gold wire to gold pad, where the substrate has good bond strength, but the die does not. If bond quality is good, and then drops off rapidly, then it's probably something to do with contamination within the system
Electronics Forum | Wed Apr 16 01:40:17 EDT 2003 | praveen
Hi , We are using water wash solder paste to solder the SMT LED's manufactured by Chicago Miniature lamp (CMD93-21 & 22)and Kingbright. Achieving the solder fillet , wetting has no issue but we observe high fallout at the functional testing. If we do
Electronics Forum | Tue Feb 08 04:27:55 EST 2011 | thomas111
hi, I am a Hardware designer . One of my products is undergoing a Reliability test in which a resistor shows a high value on board from its specified value .However it retains the original value when its cooled under room temperature. The resistor
Electronics Forum | Mon Sep 09 11:18:23 EDT 2013 | shirjer
We have a Vansco system on our 2005 Alpine Coach motor home. We have an intermittent outage problem with the 12V lighter socket. I can plug something in, like the tire sensor monitor, or the GPS, and after I remove it, the outlet no longer works, n
Electronics Forum | Thu Oct 08 01:07:46 EDT 2009 | tpappano
I have used 1A33 for many years with excellent results on through-hole pcbs in equipment subjected to very hot and very cold environments. Because 1A33 continues to harden with time, I assumed it would simply not be usable on smt boards, cracking t