Electronics Forum | Fri Feb 04 09:23:21 EST 2000 | Casimir Budzinski
If No-Clean flux does not need to be cleaned, then why do I get readings of up to 27(ug NaCl/sq in) on boards that are not washed, up to 23.4(ug NaCl/sq in) on boards washed with DI water only and from 1.2 to 10.1(ug NaCl/sq in) on boards washed with
Electronics Forum | Mon Feb 05 17:06:50 EST 2007 | George
Thank you Dave...always helpful....
Electronics Forum | Tue Jun 20 07:26:45 EDT 2017 | emeto
Thank you for the detailed input. That gave me material to think on.
Electronics Forum | Tue May 23 12:18:25 EDT 2000 | mike weekes
Which companies would you consider for protective coatings, (conformal coating) and other levels of protection? I am taking a fresh look at alternatives. Know any good tests for testing compatability of coating with flux - aqueous or no clean? SMT
Electronics Forum | Mon Jun 19 07:59:01 EDT 2017 | emeto
Hello, I am planning to use a water wash flux. As this is new to me, would you guys share what should I be aware of? I know cleaning PCBs itself presents issues. If you can share your experience so I can prepare better, it would be great.
Electronics Forum | Mon Feb 05 11:31:37 EST 2007 | davef
While you're waiting for others to reply, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=19507
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Wed Mar 01 16:59:44 EST 2000 | Dave F
Robert: Expect a 0.033" raw ball to be within 0.022" of the pad, after reflow. To be clear, that�s not a matter of shrinking by 33%. The volume of solder on the pad is the same as the volume of solder in the raw ball. It�s just that the solder is
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t