Electronics Forum | Wed Jun 13 17:18:02 EDT 2001 | mcox
Genny Thanks for the effort; I had actually called this company however they did not have any documentation for the Piglet format. Thanks Anyhow Mike
Electronics Forum | Thu May 01 18:01:38 EDT 2003 | jym2000
Just take care about reflow profile with this kind of product, you can get a bad-formation in your PCB (Flexcable or your flexcircuit) however you want to call... This bad-formations looks like a solderballs (Microscopio) Regards Jesus
Electronics Forum | Wed Jul 14 12:43:13 EDT 2004 | Daan Terstegge
There are as many CAD formats as there are BOM formats, but you should really try SMT-Maestro as it may fit your needs perfectly. The program is available from http://www.smtinfo.net/smtmaestro/smtmaestro.html
Electronics Forum | Sun Aug 22 08:16:45 EDT 2004 | Alexei
I need to know MyData File Format. I need to understand their codes... Please help me. S.O.S.
Electronics Forum | Mon Nov 22 12:51:22 EST 2004 | smokejumper
The basic answer is. Any mydata machine can tranfer files using mount file format (mydatas orignal asii format).
Electronics Forum | Sun Jun 05 21:48:05 EDT 2005 | KEN
bright tin has demonstrated remarkable reduction in wisker formation. Organic inoculations and plating thickness are two very important characteristics in wisker formation.
Electronics Forum | Thu Nov 03 13:35:46 EST 2005 | Amol
the copper forms intermetallics with tin to get Cu3Sn and Cu6Sn5. thus intermetallics formation consumes Cu and depends upon the cooling rate, faster the cooling rate, lesser the intermetallic formation
Electronics Forum | Wed Mar 29 08:21:07 EST 2006 | aj
All, I am trying to assertain if our Dross Formation on the Wave Solder Machine is in line with others. I estimate that we generate about 30 kgs/monthly in a 550kg bath. Any replies appreciated. aj
Electronics Forum | Tue Nov 14 02:53:05 EST 2006 | saaitk
Thanks for your input folks. I will have to get back to our customer regarding the analysis as it was them that carried it out. If I can get more details then I will post them. For my own benefit, is phosphorus crystal formation to be expected using