Electronics Forum | Wed Jul 27 16:46:48 EDT 2005 | russ
I don't think that you would need to test these. Have you ever seen any evidence of solder sticking to them? We use the same material and never notice anything besides flux staying on the bottom. Would the lead absorption if any even be of a concer
Electronics Forum | Mon Jul 28 11:31:42 EDT 2008 | blnorman
Ideal situation is get a technical rep from the solder paste supplier. They know their paste better, and should be able to work out a profile based on their paste and your oven. Again, a technical rep, not the sales guy.
Electronics Forum | Mon Jul 28 14:30:22 EDT 2008 | grics
Take a look at this. Remember, these are only guidlines and can not replace any paste specs. As Real Chunks said, a profiler will be of HUGE help. We use this to determine what our top side temps are and to see if we have any problems with heat sen
Electronics Forum | Fri Aug 01 21:10:35 EDT 2008 | leo_dektec
You can keep only the 5th zone as the reflow zone. And lower the first two zones to keep a good ramping rate. Meanwhile,please note the ting temperature in software or control panel is not the exact temperature in your PCB, you'd better get a KIC or
Electronics Forum | Wed Apr 26 07:37:34 EDT 2006 | amol_kane
"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from
Electronics Forum | Wed Apr 26 07:37:52 EDT 2006 | amol_kane
"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from
Electronics Forum | Wed Apr 26 01:18:33 EDT 2006 | ge_lim
Hi We are in the process of developing a lead free product to be used in a non lead free selective soldering machine, i do have concern in these, and hope you guy can share your experienced expert opinion: 1. What does it take to convert to lead fre
Electronics Forum | Wed Apr 26 09:48:32 EDT 2006 | patrickbruneel
Checkout this link http://www.rohsusa.com/ any comments on this??
Electronics Forum | Fri Feb 09 12:31:35 EST 2007 | realchunks
Ask Brain Toleno at "circuitsassembly.com/blog" He's a smart guy and works as team lead at Henkel Loctite. Just don't take him out for drinks.
Electronics Forum | Fri Feb 09 02:30:50 EST 2007 | Muhammad Haris
What are Resins, Solvents, Activators, and Thickening Agents in Solder Paste and what are their helpful and harmful effects? AND What are the purposes/properties and effects of Sn(Tin), Pb(Lead), Ag(Silver), Bi(Bismuth), In(Indium), Cu(Copper), Ni(